Evaluation of LaSr 2 Fe 2 CrO 9-δ as a Potential Electrode for Symmetrical Solid Oxide Fuel Cells

qiang zhou,chun yuan,da han,ting luo,junliang li,zhongliang zhan

DOI: https://doi.org/10.1016/j.electacta.2014.04.104

IF: 6.6

2014-01-01

Electrochimica Acta

Abstract:Structure stability and electrical conductivity of LaSr2Fe2CrO9-δ were investigated in air and in hydrogen to explore its potential applications as symmetrical electrodes for solid oxide fuel cells. X-Ray diffraction measurements showed that LaSr2Fe2CrO9-δ was essentially stable despite the presence of minor LaSrFeO4 impurities after heat-treated in humidified hydrogen at 800°C. LaSr2Fe2CrO9-δ-based symmetrical fuel cells fabricated on LSGM electrolyte substrates via screen printing achieved a maximum power density of 224 mW cm−2. After using a composite electrode (50 wt% LaSr2Fe2CrO9-δ–50 wt% Gd0.2Ce0.8O2-δ), both the anode and the cathode polarization resistances decreased. The maximum power density of symmetrical fuel cells using LaSr2Fe2CrO9-δ–Gd0.2Ce0.8O2-δ composite electrodes increased to 264 mW/cm2 and the corresponding total cell polarization resistance was 0.454Ω cm2 at 800°C with humidified hydrogen fuels and ambient air oxidants.