Abstract:Single-phase Li0.5-0.5xZnxFe2.5-0.5xO4 (where x=0.0, 0.2, 0.3, 0.4, 0.5 and 0.8) nanofibers with diameters of 50 similar to 100 nm were successfully fabricated via electrospinning technique in combination with subsequent heat treatment using polyvinylpyrrolidone, nickel nitrate, zinc nitrate and ferric nitrate as principal raw material. The thermal decomposition process of as-spun precursor nanofibers and the influences of the calcination temperature and chemical composition on the crystal structure, micromorphology and magnetic properties of the prepared nanofiber samples were investigated by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and vibrating sample magnetometer. The results indicate that the pure crystalline LiZn ferrite nanofibers are basically formed when the precursor nanofibers are calcined at 350 degrees C for 2 h. As the calcination temperature increases from 350 to 600 degrees C, the average grain size of Li0.35Zn0.3Fe2.35O4 nanofibers ranges from 13.0 to 47.5 nm and the micromorphology evolves toward a chain-like structrue. The saturation magnetization of the samples monotonously increases from 39.7 to 84.5 A.m(2).kg(-1), while the coercivity increases initially, reaches a maximun value of 12.6 kA.m(-1) at 550 C and then decreases, which reveals that the magnetic single-domain critical size of Li0.35Zn0.3Fe2.35O4 nanofibers may be around 35 nm. The lattice constant of as-prepared Li0.5-0.5xZnxFe2.5-0.5xO4 nanofibers calcined at 500 degrees C for 2 h exhibits an almost linear increase with increasing x and complies with Vegard's law. The coercivity of these nanofiber samples gradually decreases from 17.1 kA.m(-1) for x=0.0 to 2.4 kA.m(-1) for x=0.8, and the saturation magnetization firstly increases to 74.7 A.m(2).kg(-1) with the value of x up to 0.3 and then decreases beyond this limit. Compared to the nanoparticle counterparts prepared under similar conditions, the LiZn ferrite nanofibers have a relatively high coercivity due to their large shape anisotropy. These LiZn ferrite nanofibers have potential application in many fields such as nanoelectronic devices, sensitive devices, microwave absorbers, and biomedicine.

Preparation and Xylene‐Sensing Properties of Co3O4 Nanofibers

Preparation and morphology controlling of Co3O4 nanostructures and their gas-sensing properties

Electrospinning Preparation of Pd@Co3O4-ZnO Composite Nanofibers and Their Highly Enhanced VOC Sensing Properties

Electrospinning Route for Α-Fe2o3 Ceramic Nanofibers and Their Gas Sensing Properties

Pt-Cr2O3-WO3 composite nanofibers as gas sensors for ultra-high sensitive and selective xylene detection

Synthesis and acetone sensing properties of Ce-doped ZnO nanofibers

Rough SmFeO3 nanofibers as an optimization ethylene glycol gas sensor prepared by electrospinning

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Fabrication and Characterization of LaCoO3 Nanofibers Via an Electrospinning Technique

Exciton quenching and ferromagnetism-to-ferrimagnetism crossover in diluted magnetic semiconducting Zn1-xCoxO nanogranular nanofibers

Preparation of Eu, Li co-doped ZnO red fluorescence nanofibers by electrospinning and their characterization

Cobalt monosulfide nanofibers: ethanol sensing and magnetic properties

Nickel-doped tin oxide hollow nanofibers prepared by electrospinning for acetone sensing

Electrospinning Preparation, Structural and Magnetic Properties of Li0.5-0.5xznxfe2.5-0.5xo4 Nanofibers

Detection of Xylene Using Ni(OH)2-Enhanced Co3O4 Nanoplate Via P–n Junctions

Coaxial electrospinning Fe2O3@Co3O4 double-shelled nanotubes for enhanced ethanol sensing performance in a wide humidity range

Construction of Co3O4/SnO2 Yolk-Shell Nanofibers for Acetone Gas Detection

Highly Responsive and Selective Ethanol Gas Sensor Based on Co3O4-Modified SnO2 Nanofibers

Preparation and Characterization of Novel Fe2o3-Flaky Coated Carbon Fiber by Electrospinning and Hydrothermal Methods

Fabrication and characterization of polycrystalline WO3 nanofibers and their application for ammonia sensing

Enhanced Xylene Detection Performance of Colloidal Quantum Dots Modified Tungsten Oxide Composites