Abstract:Ti(Fe, Co, Ni)Sb-based half-Heusler alloys were synthesized by levitation melting, ball milling and SPS.The carrier concentration and the density of states effective mass were significantly increased by Co doping.The lattice thermal conductivity was decreased due to the point defect scattering induced by Hf alloying.●Peak ZTs of ∼0.65 and ∼0.85 at 973 K were achieved in n-type and p-type Ti(Fe, Co, Ni)Sb-based materials, respectively.TiFe0.5Ni0.5Sb-based half-Heusler compounds have the intrinsic low lattice thermal conductivity and the adjustable band structure. Inspired by the previously reports to achieve both p- and n-type components by tuning the ratio of Fe and Ni based on the same parent TiFe0.5Ni0.5Sb, we selected Co as the amphoteric dopants to prepare both n-type and p-type pseudo-ternary Ti(Fe, Co, Ni)Sb-based half-Heusler alloys. The carrier concentration, as well as the density of states effective mass was significantly increased by Co doping, contributing to the enhanced power factor of 1.80 mW m-1 K-2 for n-type TiFe0.3Co0.2Ni0.5Sb and 2.21 mW m-1 K-2 for p-type TiFe0.5Co0.15Ni0.35Sb at 973 K. Combined with the further decreased lattice thermal conductivity due to the strain field and mass fluctuation scattering induced by alloying Hf on the Ti site, peak ZTs of 0.65 in n-type Ti0.8Hf0.2Fe0.3Co0.2Ni0.5Sb and 0.85 in p-type Ti0.8Hf0.2Fe0.5Co0.15Ni0.35Sb were achieved at 973 K, which is of great significance for the thermoelectric power generation applications.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S2352847820305396-fx1_lrg.jpg">Download : Download high-res image (316KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S2352847820305396-fx1.jpg">Download : Download full-size image</a></li></ol>

Band engineering of high performance p-type FeNbSb based half-Heusler thermoelectric materials for figure of merit zT > 1

Realizing high figure of merit in heavy-band p -type half-Heusler thermoelectric materials

High Band Degeneracy Contributes to High Thermoelectric Performance in p-Type Half-Heusler Compounds

TaFeSb-Based Half-Heusler Thermoelectrics with High zT > 1 through the Alloying Effect

Enhancing Thermoelectric Performance of FeNbSb Half-Heusler Compound by Hf-Ti Dual-Doping

Realizing both n- and p-types of High Thermoelectric Performance in Fe1-xNixTiSb half-Heusler compounds

Enhanced Thermoelectric Performance in the N-Type NbFeSb Half-Heusler Compound with Heavy Element Ir Doping

Performance Advancements in P-Type TaFeSb-Based Thermoelectric Materials through Composition and Composite Optimizations

Discovery of TaFeSb-based Half-Heuslers with High Thermoelectric Performance

High-performance Half-Heusler Thermoelectric Materials Hf1−x ZrxNiSn1−ySby Prepared by Levitation Melting and Spark Plasma Sintering

Stronger Phonon Scattering by Larger Differences in Atomic Mass and Size in P-Type Half-Heuslers Hf1−xTixCoSb0.8Sn0.2

Realizing both n- and p-types of high thermoelectric performance in Fe<sub>1−x</sub>Ni<sub>x</sub>TiSb half-Heusler compounds

High Efficiency Half‐Heusler Thermoelectric Materials for Energy Harvesting

Design of High‐Performance Disordered Half‐Heusler Thermoelectric Materials Using 18‐electron Rule

Synergistic Band and Defect Engineering in ZrNiSn Alloys Via Ni-Vacancy Regulation for Realizing High Thermoelectric Performance

High Thermoelectric Figure of Merit by Resonant Dopant in Half-Heusler Alloys

Thermoelectric Properties of N-Type ZrNiPb-Based Half-Heuslers

Enhanced thermoelectric performance in Ti(Fe, Co, Ni)Sb pseudo-ternary Half-Heusler alloys

Theoretical Maximum Thermoelectric Performance of p‐Type Hf‐ and Zr‐Doped NbFeSb Half‐Heusler Compounds

Engineering the Thermoelectric Transport in Half‐Heusler Materials through a Bottom‐Up Nanostructure Synthesis

Sn Doped FeNbSb Half-Heusler Compounds for Tuning Thermoelectric Performance