Abstract:Ti(Fe, Co, Ni)Sb-based half-Heusler alloys were synthesized by levitation melting, ball milling and SPS.The carrier concentration and the density of states effective mass were significantly increased by Co doping.The lattice thermal conductivity was decreased due to the point defect scattering induced by Hf alloying.●Peak ZTs of ∼0.65 and ∼0.85 at 973 K were achieved in n-type and p-type Ti(Fe, Co, Ni)Sb-based materials, respectively.TiFe0.5Ni0.5Sb-based half-Heusler compounds have the intrinsic low lattice thermal conductivity and the adjustable band structure. Inspired by the previously reports to achieve both p- and n-type components by tuning the ratio of Fe and Ni based on the same parent TiFe0.5Ni0.5Sb, we selected Co as the amphoteric dopants to prepare both n-type and p-type pseudo-ternary Ti(Fe, Co, Ni)Sb-based half-Heusler alloys. The carrier concentration, as well as the density of states effective mass was significantly increased by Co doping, contributing to the enhanced power factor of 1.80 mW m-1 K-2 for n-type TiFe0.3Co0.2Ni0.5Sb and 2.21 mW m-1 K-2 for p-type TiFe0.5Co0.15Ni0.35Sb at 973 K. Combined with the further decreased lattice thermal conductivity due to the strain field and mass fluctuation scattering induced by alloying Hf on the Ti site, peak ZTs of 0.65 in n-type Ti0.8Hf0.2Fe0.3Co0.2Ni0.5Sb and 0.85 in p-type Ti0.8Hf0.2Fe0.5Co0.15Ni0.35Sb were achieved at 973 K, which is of great significance for the thermoelectric power generation applications.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S2352847820305396-fx1_lrg.jpg">Download : Download high-res image (316KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S2352847820305396-fx1.jpg">Download : Download full-size image</a></li></ol>

TaFeSb-Based Half-Heusler Thermoelectrics with High zT > 1 through the Alloying Effect

Alloyed triple half-Heuslers: a route toward high-performance thermoelectrics with intrinsically low lattice thermal conductivity

Band engineering of high performance p-type FeNbSb based half-Heusler thermoelectric materials for figure of merit zT > 1

Unique Role of Refractory Ta Alloying in Enhancing the Figure of Merit of NbFeSb Thermoelectric Materials

Discovery of TaFeSb-based Half-Heuslers with High Thermoelectric Performance

Enhanced Thermoelectric Performance in Hf-Free p-Type (Ti, Zr)CoSb Half-Heusler Alloys

Engineering the Thermoelectric Transport in Half‐Heusler Materials through a Bottom‐Up Nanostructure Synthesis

High Band Degeneracy Contributes to High Thermoelectric Performance in p-Type Half-Heusler Compounds

Design of High‐Performance Disordered Half‐Heusler Thermoelectric Materials Using 18‐electron Rule

Enhancement in Thermoelectric Properties of ZrNiSn-based Alloys by Ta Doping and Hf Substitution

Half-Heusler alloys as emerging high power density thermoelectric cooling materials

Performance Advancements in P-Type TaFeSb-Based Thermoelectric Materials through Composition and Composite Optimizations

High Thermoelectric Figure of Merit by Resonant Dopant in Half-Heusler Alloys

Enhanced thermoelectric performance in Ti(Fe, Co, Ni)Sb pseudo-ternary Half-Heusler alloys

A novel valence-balanced double half-Heusler Ti2Zr2Hf2NbVFe5Ni3Sb8 alloy by high entropy engineering

Realizing high figure of merit in heavy-band p -type half-Heusler thermoelectric materials

Enhanced thermoelectric performance of n-type TiCoSb half-Heusler by Ta doping and Hf alloying

Enhancing Thermoelectric Performance of FeNbSb Half-Heusler Compound by Hf-Ti Dual-Doping

Stronger Phonon Scattering by Larger Differences in Atomic Mass and Size in P-Type Half-Heuslers Hf1−xTixCoSb0.8Sn0.2

Structure and thermoelectric properties of half-Heusler-like TiFeCu Sb alloys

Alloying To Increase The Band Gap For Improving Thermoelectric Properties Of Ag2te