Abstract:In this study, an improved peak figure‐of‐merit of 0.55 at 973 K is realized in p‐type MNiSn (M=Hf, Zr, Ti) half‐Heusler materials, which exceed the state‐of‐the‐art p‐type MNiSn by 100%. The advanced p‐type transport is ascribed to the modulation of defects, as evidenced by calculating the formation energies from first principles and refining the diffraction patterns. The thermoelectric figure‐of‐merit (zT) of p‐type MNiSn (M = Ti, Zr, or Hf) half‐Heusler compounds is lower than their n‐type counterparts due to the presence of a donor in‐gap state caused by Ni occupying tetrahedral interstitials. While ZrNiSn and TiNiSn, have been extensively studied, HfNiSn remains unexplored. Herein, this study reports an improved thermoelectric property in p‐type HfNi1−xCoxSn. By doping 5 at% Co at the Ni sites, the Seebeck coefficient becomes reaching a peak value exceeding 200 μV K−1 that breaks the record of previous reports. A maximum power factor of ≈2.2 mW m−1 K−2 at 973 K is achieved by optimizing the carrier concentration. The enhanced p‐type transport is ascribed to the reduced content of Ni defects, supported by first principle calculations and diffraction pattern refinement. Concomitantly, Co doping also softens the lattice and scatters phonons, resulting in a minimum lattice thermal conductivity of ≈1.8 W m−1 K−1. This leads to a peak zT of 0.55 at 973 K is realized, surpassing the best performing p‐type MNiSn by 100%. This approach offers a new method to manipulate the intrinsic atomic disorder in half‐Heusler materials, facilitating further optimization of their electronic and thermal properties.

Half-Heusler compounds for thermoelectric energy conversion

Thermoelectric Performance of Half-Heusler Compounds TiNiSn and TiCoSb

High Performance P-Type Half-Heusler Thermoelectric Materials

Half-Heusler Compounds: Promising Materials For Mid-To-High Temperature Thermoelectric Conversion

n-Type TaCoSn-Based Half-Heuslers as Promising Thermoelectric Materials

High Efficiency Half‐Heusler Thermoelectric Materials for Energy Harvesting

Enhancing the Thermoelectric Properties via Modulation of Defects in P‐Type MNiSn‐Based (M = Hf, Zr, Ti) Half‐Heusler Materials

Half Heusler Alloys for Efficient Thermoelectric Power Conversion

Half-Heusler thermoelectric materials: NMR studies

Improved Thermoelectric Performance in N-Type Half-Heusler NbCoSn by Heavy-Element Pt Doping

Search for Thermoelectrics with High Figure of Merit in half-Heusler compounds with multinary substitution

Power generation from n-type NbCo1−xNixSn and p-type NbFe1−xMnxSb ternary half-Heusler compounds: from materials development to module fabrication

Thermoelectric Properties and N - to P -Type Conversion of Co-Doped ZrNiSn-Based Half-Heusler Alloys

Improving the thermoelectric performance of double half-Heusler compounds ZrNi(In,Sb)

High-performance Half-Heusler Thermoelectric Materials Hf1−x ZrxNiSn1−ySby Prepared by Levitation Melting and Spark Plasma Sintering

Realizing high figure of merit in heavy-band p -type half-Heusler thermoelectric materials

Enhanced thermoelectric performance of n-type TiCoSb half-Heusler by Ta doping and Hf alloying

Thermoelectric Properties of N-Type Half-Heusler NbCoSn with Heavy-Element Pt Substitution

Lanthanide Contraction As a Design Factor for High‐Performance Half‐Heusler Thermoelectric Materials

Band Structures and Transport Properties of High-Performance Half-Heusler Thermoelectric Materials by First Principles

Band engineering of high performance p-type FeNbSb based half-Heusler thermoelectric materials for figure of merit zT > 1