Abstract:The polycrystalline IN713C produced via investment casting is one of the widely-used nickel-based superalloy in automotive and aerospace industries. This alloy, however, has an apparent inhomogeneous microstructure generated during casting and contains dendritic structure that gives rise to strain localisation during loading. Yet, the effect of dendrite structure, grain size and shape as well as crystallographic orientation, which directly influence fatigue property and deformation micromechanism in the components, is rarely studied. In the present study, IN713C cast bars are tailored with three different grain structures, i.e., transition, equiaxed and columnar, with substantial grain size variations. The produced bars were tested under strain controlled LCF (Low Cycle Fatigue) and stress controlled HCF (High Cycle Fatigue) conditions at 650 °C. The results showed that most of fatigue cracks initiated from casting porosities and fatigue life extended in the microstructure with a small grain size during both HCF and LCF loadings. It is also demonstrated that fatigue striations were mainly observed within dendrite areas during crack propagation, whereas the higher GND (Geometrically Necessary Dislocation) density were predominantly observed in the interdendrite areas. Here, we propose a concept of 'Crack Propagation Unit (CPU)' for better description of deformation mechanism at local scale during fatigue loading by combining fracture surface characteristic methodology and dislocation distribution analyses within the dendrite structural unit. Furthermore, this model to understand the deformation micromechanism can provide a new perspective on the interpretation of Hall-Petch relationship in casting materials that contain dendritic structure. This is further demonstrated via direct correlation of the high crack propagation resistance with the crack path divergence instead of the dislocation pile-up at the grain boundary or in-between the γ/ γ' channels. Moreover, by utilising serial sectioning method followed by layered EBSD scanning, quasi-3-D grain orientation mappings were obtained, and crystallographic texture information were directly correlated with the fracture surface observations. This allowed an investigation of the influence of orientation of individual grains and micro/macro texture on crack propagation rate. The critical stage of crack propagation in fatigue life and its correlations with microstructural features is established, offering potential practical applications by controlling the investment casting process parameters.

Grain Size Effect on the Small Fatigue Crack Initiation and Growth Mechanisms of Nickel-Based Superalloy GH4169

Grain Size Effect on Multi-Scale Fatigue Crack Growth Mechanism of Nickel-based Alloy GH4169

Influence of Grain Size on the Small Fatigue Crack Initiation and Propagation Behaviors of a Nickel-Based Superalloy at 650 °C

Small Fatigue Crack Initiation and Growth Mechanisms of Nickel-Based Superalloy GH4169 at 650 °C in Air

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Effects of Grain Sizes on Small Fatigue Crack Growth of GH4169 Ni-base Alloy

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Micro-notch Size Effect on Small Fatigue Crack Propagation of Nickel-Based Superalloy GH4169

Effect of Stress Ratio on the Fatigue Crack Propagation Behavior of the Nickel-based GH4169 Alloy

The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy

Microstructural size effect on the notch fatigue behavior of a Ni-based superalloy using crystal plasticity modelling approach

Grian Size Effect on the Initiation and Propagation of Small Fatigue Crack of GH4169 Alloy at Room Temperature and 650 ℃

Microstructural insights into fatigue short crack propagation resistance and rate fluctuation in a Ni-based superalloy manufactured by Laser powder bed fusion

Crack initiation mechanisms and life prediction of GH4169 superalloy in the high cycle and very high cycle fatigue regime

Fatigue Life Prediction of Nickel-Based GH4169 Alloy on the Basis of a Multi-Scale Crack Propagation Approach

Study of Fatigue Crack Initiation and the Propagation Mechanism Induced by Pores in a Powder Metallurgy Nickel-Based FGH96 Superalloy

Investigations of micro-notch effect on small fatigue crack initiation behaviour in nickel-based alloy GH4169: Experiments and simulations

Investigation of Fatigue Small Crack Propagation Behavior in Superalloy FGH96 under Different Stress Ratios

Research on the influence of microstructure on the initiation and propagation of micro-cracks of superalloy GH4169

Microstructural Evolution and Formation of Fine Grains During Fatigue Crack Initiation Process of Laser Powder Bed Fusion Ni-based Superalloy

Fatigue crack nucleation behavior in nickel-based PM alloy