Sol–gel Synthesis and Characterisation of La Doped (1−x)batio3–x(bi0·5k0·5)tio3ptcr Ceramics

C. Zhang,L. Z. Di,C. H. Ding,L. X. Lu,T. Zhai,D. A. Yang

DOI: https://doi.org/10.1179/1753555714y.0000000224

2014-01-01

Materials Technology

Abstract:As a promising material for lead free positive temperature coefficient of resistivity (PTCR) ceramics, La doped (1-x) BaTiO3-x(Bi0.5K0.5) TiO3 [(12x) BT-xBKT] samples with 0 <= x <= 0.04 were prepared by a citrate-nitrate sol-gel method. The corresponding gels were heated at different temperatures (500, 600 and 800 degrees C) to study the conditions necessary for the formation of the pure BT-BKT. Single phased perovskite powders with average particles size of 70 nm were obtained by heating the precursor gels at 800 degrees C for 1 h in air. The crystal structure, microstructure and the electrical properties of La doped BT-BKT samples were studied. When the content of La was 0.2 mol.-%, the 0.99BT-0.01BKT ceramic showed the lowest rho(RT). With increasing addition of BKT, the Curie temperature (T-c) and the room temperature resistivity (rho(RT)) increased. When the content of BKT was 4 mol.-%, the sample sintered in air atmosphere still showed good PTCR behaviours with T-c = 143 degrees C, RT=1.1 x 10(4) Omega cm and I-g (rho(max)/rho(min))=3.76.