Electrochemical Analysis on Intergranular Corrosion of Austenitic Stainless Steel Weld in Molten Nitrate Salt
Noparat Kanjanaprayut,Thamrongsin Siripongsakul,Panya Wiman,Wannapha Issaard,Thanasak Nilsonthi,Piyorose Promdirek
DOI: https://doi.org/10.3390/met14111284
IF: 2.695
2024-11-13
Metals
Abstract:An investigation of intergranular corrosion (IGC) sensitization in molten nitrate salts of austenitic stainless steel welds of AISI 304, AISI 304H, and AISI321 produced by GTAW with ER 308L and ER 347 fillers was performed. The degree of sensitization (DOS) to IGC was assessed using a double loop electrochemical potentiokinetic reactivation and pitting potential. It was found that DOS levels in weld zones were quite low, not exceeding 15%, while those in HAZs were up to 60% after exposure at 600 °C for 300 h. The low DOS levels were due to low carbide precipitation. However, another cause of DOS was the delta-ferrite to sigma transformation in weld zones. Linear sweep voltammetry was used to quantify the sigma phase.
materials science, multidisciplinary,metallurgy & metallurgical engineering