Environment assisted cracking of 308L weld metal in high temperature water
Jiamei Wang,Tianyu Zhu,Yaolei Han,Jinna Mei,Fei Xue,Kai Chen,Donghai Du,Peter L. Andresen,Lefu Zhang,Miaomiao Zhang
DOI: https://doi.org/10.1016/j.jnucmat.2021.153275
IF: 3.555
2021-12-01
Journal of Nuclear Materials
Abstract:The environment assisted cracking (EAC) behavior, including stress corrosion cracking (SCC) and corrosion fatigue (CF), of a low carbon 308L stainless steel weld metal was evaluated in high temperature water. The effects of thermal aging (400°C for 10,000h) on the crack growth rate (CGR) are discussed. Experimental results reveal an environmental acceleration effect on CGRs with decreasing loading frequency, and the environmental enhancement factor reached a value of 50 when the frequency was decreased to 0.00001 Hz. The 308L weld metal showed excellent SCC resistance regardless of the thermal aging or water chemistry, which is related to the low carbon content and well-controlled duplex microstructure. After thermal aging, the ferrite/austenite (γ/δ) phase boundaries show negligible sensitization, consistent with the low carbon concentration. No preference of the γ/δ crack path and no elevated EAC either with thermal aging or in oxidizing water was attributed to the no sensitization of the γ/δ boundaries before and after thermal aging.
materials science, multidisciplinary,nuclear science & technology