Abstract:Zinc oxide (ZnO) varistors, which are produced by sintering ZnO powder together with small additives of Bi2O3, Co3O4, Sb2O3 and other oxides, are popular ceramic semiconductor devices and widely used in electric circuits and systems as voltage-clamping or surge-arrester owing to their extremely nonlinear current–voltage characteristics. The reliability of ZnO varistors is the most important consideration, and researches are mainly focus on the material properties of ZnO body and the effects of additives, such as ZnO grain size and the surrounding additive-rich insulating barriers. However, the manufacturing of electrodes still remains the traditional silver baking process, and few people investigate the effects of electrodes on the reliability of devices. In this paper, we propose a novel electrodes manufacture process using magnetron sputtering technology, and investigate the reliability of devices comparing to silver baking process. Two groups of samples with diameters of 20mm were prepared by silver baking and magnetron sputtering process respectively. The nonlinear voltage, nonlinear coefficient, and leakage current parameters were measured by the metal oxide varistor meter typed TTK-168; the energy absorption capacities were measured by a lightning current surge generator with 8/20μs impulse waves; the adhesive strength of electrodes was measured by a dynamometer; the microstructures of the samples were examined using Scanning Electron Microscope, and the change ratio of nonlinear voltages at an environment of 125°C after 100h was chosen as the main reliability parameter. Results show that the sputtered electrodes could improve the reliability of samples by reducing the change ratio from 1.32% to 0.61%, with other parameters exceeding the silver baking samples at the same time. This enhancement is benefit from the good interface between sputtered electrodes and ZnO substrate as well as the low temperature during magnetron sputtering process.

Nanosize Powders of Zinc Oxide Produced by Electrical Explosion of Zinc Wires

Nanopowder Production by Gas-Embedded Electrical Explosion of Wire

Nano-powder Production by Electrical Explosion of Wires

Study of nanopowder production by gas-embeded electrical explosion of wire

Two Different Modes Of Wire Explosion For Nano-Powder Production

Numerical simulation of pulsed wire discharge for nano-powder production

Behavior of exploding wires

Reliability enhancement of zinc oxide varistors using sputtered silver electrodes.

Study on the Evolution of Wire Explosion in Ambient Gas for Nano-powder Production

ZnO Nanowire-Based Corona Discharge Devices Operated under Hundreds of Volts

Field Emission from Zinc Oxide Nanostructures and Its Degradation

Circuit Simulation Of The Behavior Of Exploding Wires For Nano-Powder Production

Properties of ZnO Varistors Prepared with Nano-Sized Powders

Evolution of the Exploding Titanium Wire in 5-50 Kpa Ambient Gas

Controlled Crystal Growth of ZnO Nanobelts by Chemical Vapor Deposition Method

Compact metal nano-powder generator of 273 MW average power and synthesis of copper nano-powder

Field Emission Properties of Zinc Oxide Nanowires Fabricated by Thermal Evaporation

Electron beam irradiation enhanced varistor properties in ZnO nanowire

Growth and Electrical Properties of Zinc Oxide Nanowires.

Study on Electrical Explosion of Bare and Insulation Coated Tungsten Wires

An Electric Discharge Device for Producing Nanoparticles from Conductive Granules