Abstract:It is predicted that the thickness of a coating has major effects on a substrate in terms of mechanical and thermal properties. In this study, an Al 2 O 3 –ZrO 2 –SiO 2 slurry was prepared as a coating material, which formed an alumina–zirconia–mullite composite coating after sintering. The alumina–zirconia–mullite composite coating was coated on a zirconia substrate to generate compressive stress in the coating due to the mismatch of the coefficient of thermal expansion (CTE). A series of coated samples with different coating thicknesses from ∼10 μm to ∼200 μm were prepared to investigate the effects of coating thickness. The residual compressive stress, thermal conductivity, CTE, and Young's modulus of the coating material were determined by relative methods, and the flexural strength of the coated and uncoated samples was measured by 3-point bending. The strength of the coated samples was 1362.98 ± 30.29 MPa, which is a 54.07% enhancement compared to the uncoated samples. The thermal conductivity of the coated samples was also increased compared to that of the uncoated samples. For a given thickness of the substrate of 2 mm, there was an optimum thickness of the coating of 90 μm, which showed the greatest strength compared to the other samples. Coatings that were too thin or too thick did not show the best reinforcement. Moreover, the porosity of the coated samples was also determined and discussed in this study. Comparison samples without SiO 2 were also manufactured, and their flexural strength and thermal conductivity were found to not be as good as the samples with SiO 2 .

A Zirconium Carbide Coating on Graphite Prepared by Reactive Melt Infiltration

Dense Submicron-Sized ZrC – W Composite Produced by Reactive Melt in Fi Ltration at 1200 ° C

PREPARATION AND CHARACTERIZATION OF CaZrO3 COATING ON GRAPHITE FOR TiNi ALLOY MELTING

Ablation Resistance of ZrB2-SiC-Si Composite Coatings Applied on Graphite Substrate by Spark Plasma Sintering

High Temperature Decomposition Behavior of CaZrO3 Coating on Graphite for TiNi Alloy Melting

Ablation behavior and mechanism of SiCnw modified SiC-ZrC coating for graphite under a plasma ablation flame

Improvement in the thermal conductivities and bending strengths of graphite film/Cu composites by matrix alloying with Zr

Microstructure Analysis of Zirconium Carbide Layer on Pyrocarbon-Coated Particles Prepared by Zirconium Chloride Vapor Method

Influence of ZrC on the Microstructure of Its Surrounding Resin-Based Carbon at High Temperature

Effects of HfC/PyC Core-Shell Structure Nanowires on the Microstructure and Mechanical Properties of Hf1-xZrxC Coating

ZrSi2-SiC/SiC Anti-Oxidant Coatings Prepared on Graphite Spheres by Two-Step Pack Cementation Process

Microstructure, surface stress and surface temperature response of ZrB2–SiC based coatings

High-temperature Diffusion Behavior of ZrC in C Matrix and Its Promotion on Graphitization

Preparation and Characterization of Zirconium Carbide Coating on Coated Fuel Particles

Preparation and Tribological Properties of Graphene-Based Coatings on Tungsten Carbide

Research on Microstructure and Oxidation Resistant Property of ZrSi2-SiC/SiC Coating on HTR Graphite Spheres

Microstructure and Ablation Behavior of W/ZrC/SiC Coating on C/C Composites Prepared by Reactive Melt Infiltration and Atmospheric Plasma Spraying

Effect of Graphene on the Microstructure and Mechanical Properties of WC-Based Cemented Carbide

Effect of silicon/graphite ratio and temperature on oxidation protective properties of SiC/ZrB2–SiC coatings prepared by pack cementation

Quantification of the Carbon-Coating Effect on the Interfacial Behavior of Graphite Single Particles

Thickness effect of an alumina–zirconia–mullite composite coating on the properties of zirconia