Modification of the Core–shell Ratio to Prepare PB-g-(MMA-co-St-co-GMA) Particle-Toughened Poly(butylene Terephthalate) and Polycarbonate Blends with Balanced Stiffness and Toughness

Yang Guo,Shulin Sun,Huixuan Zhang

DOI: https://doi.org/10.1039/c4ra08646e

IF: 4.036

2014-01-01

RSC Advances

Abstract:Particles with a modified core–shell ratio provide an effective way to prepare polymer blends with a superior balance of toughness and stiffness.

What problem does this paper attempt to address?

Preparation of PBT/POE‐g‐GMA/PP Ternary Blends with Good Rigidity–toughness Balance by Core–shell Particles

Mengyao Shang,Henglun Cheng,Baoqing Shentu,Zhixue Weng

DOI: https://doi.org/10.1002/app.48872

IF: 3

2019-01-01

Journal of Applied Polymer Science

Abstract:ABSTRACTCompared with poly(butylene terephthalate)/glycidyl methacrylate grafted poly(ethylene–octene) (PBT/POE‐g‐GMA) binary blends, supertough PBT‐based ternary blends with little rigidity loss were successfully obtained by adding rigid polypropylene (PP) into PBT/POE‐g‐GMA blends to construct core–shell particles during melt blending. The effects of PP content and type on the phase morphology and mechanical properties of the blends were systematically investigated. Theoretical predictions and scanning electron microscopy observation showed that a core–shell structure was formed in PBT matrix with PP as the core and POE‐g‐GMA as the shell. The mechanical property tests showed that POE‐g‐GMA and PP had significant synergistic toughening effect. When PP with high melt flow index (H‐PP) was used, PBT/POE‐g‐GMA/H‐PP (70/15/15) blends possessed the highest Izod notched impact strength, which was 1.9‐fold compared with PBT/POE‐g‐GMA (70/30) binary blends, while the tensile performance loss was little. The essential work of fracture tests was performed to evaluate the fracture resistance of different samples. The results demonstrated that PBT/POE‐g‐GMA/PP ternary blends possessed much better resistance to crack propagation than PBT/POE‐g‐GMA binary blends. The decrease of interparticle distance and the fibrillation of core–shell particles activated intense matrix shear yielding, which was the reason for the high crack resistance of ternary blends. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020, 137, 48872.
Modification of the Reactive Core-Shell Particles Properties to Prepare PBT/PC Blends with Higher Toughness and Stiffness

Bin Deng,Hanxiao Lv,Shixin Song,Shulin Sun,Huixuan Zhang

DOI: https://doi.org/10.1007/s10965-017-1250-3

IF: 3.061

2017-01-01

Journal of Polymer Research

Abstract:Glycidyl methacrylate (GMA) functionalized methyl methacrylate-butadiene-styrene core-shell particles (PB-g-MSG) were prepared to toughen poly (butylene terephthalate) (PBT) and polycarbonate (PC) blends. T-dodecyl mercaptan (TDDM) was used to modify the grafting character of the core-shell particles. The addition of TDDM decreased the grafting degree, particles size and crosslinking degree of PB-g-MSG particles. At the same time, the free methyl methacrylate-co-styrene-co-glyceryl methacrylate copolymer (f-MSG) increased. The f-MSG reacted with PBT and suppressed the transesterification between PBT and PC. On the other hand, f-MSG promoted the crystallization of PBT by heterogeneous nucleation. When the TDDM content was lower than 0.76%, PB-g-MSG particles dispersed in the matrix uniformly, otherwise, agglomeration took place. The change of TDDM content in the PB-g-MSG particles influenced the toughening ability and tensile properties. When the TDDM content was 0.76%, the PBT/PC/PB-g-MSG blend showed the optimum impact toughness and yield strength, which are 908 J/m and 49.4Mpa. Fracture mechanism results indicated that cavitation induced shear yielding occurred in the PBT/PC/PB-g-MSG blend when no TDDM addition for the core-shell particles. With the addition of TDDM, the interfacial strength decreased between the PB-g-MSG core-shell particles and the matrix. So voids appeared due to debonding, which also could promote the shear yielding process.
PREPARATION AND CHARACTERISTICS OF PBA/PMMA CORE-SHELL PARTICLES AS TOUGHER

Hong FAN,Jian-li WANG

DOI: https://doi.org/10.3321/j.issn:1000-7555.2000.06.009

2000-01-01

Abstract:A series of PBA core PMMA shell particles as tougher were prepared using conventional emulsion polymerization, less emulsifier emulsion polymerization and free emulsion polymerization. It is found that the vinyl groups content of PBA rubbery core increases with the amount of cross linking agents increased and core shell ratio(mass) has great effect on the morphology of complex particles. The carboxyl quantities on the surface of core shell particles were determined by potentiometric titration. Results show that methylacrylic acid, which is loaded, is distributed on the surface of particles. The morphology of latex is determined by transmission electron microscope. The size and its distribution of latex particles were measured by LS counters particle size instrument.
Effect of Core-Shell Particles Dispersed Morphology on the Toughening Behavior of PBT/PC Blends

Bin Deng,Yang Guo,Shixin Song,Shulin Sun,Huixuan Zhang

DOI: https://doi.org/10.1007/s10965-016-1106-2

IF: 3.061

2016-01-01

Journal of Polymer Research

Abstract:Methyl methacrylate-co-styrene-co-glycidyl methacrylate grafted polybutadiene (PB-g-MSG) and styrene-co-glycidyl methacrylate grafted polybutadiene (PB-g-SG) core-shell particles were prepared to toughen poly (butylene terephthalate) (PBT) and polycarbonate (PC) blends. The compatibilization reaction between the epoxy groups of glycidyl methacrylate and the carboxyl groups of PBT induced the PB-g-SG particles dispersed in the PBT phase. On the other hand, the good miscibility between PMMA (the shell phase of PB-g-MSG) and PC induced the PB-g-MSG particles dispersed in the PC phase. The different phase morphology led to different toughening behavior. The PBT/PC/PB-g-MSG blends with the PC encapsulated morphology showed much lower brittle-ductile transition core-shell particles content (10-15 wt% or 15-20 wt%) compared with the PBT/PC/PB-g-SG blends (20-25 wt%). The difference between the toughening efficiency of the core-shell particles was due to the change of deformation mechanisms. In PBT/PC/PB-g-MSG blends, the cavitation of PB rubber phase led to the occurrence of shear yielding of the matrix. While in the PBT/PC/PB-g-SG blends, the debonding between PBT and PC interface induced the shear yielding of the matrix. The variation of the core-shell particles dispersed phase morphology also affected the crystallization properties and DMA results of the PBT/PC blends. Modification of the phase morphology provided an useful strategy to prepare PBT/PC blends with higher toughening efficiency.
In Situ Formation of the Core–Shell Particles and Their Function in Toughening PA6/SEBS-g-MA/PP Blends

Yijian Wu,Hui Zhang,Baoqing Shentu,Zhixue Weng

DOI: https://doi.org/10.1021/acs.iecr.7b02202

2017-01-01

Industrial & Engineering Chemistry Research

Abstract:This work aimed at preparing supertough PA6 blends with only a small :amount of elastomer. The PA6/SEBS-g-MA/PP blends were obtained by melt extrusion, in which the core-shell particles (PP as: core and SEBS-g-MA as shell) could be formed in situ in PA6 matrix. The morphology PA6 blends was, explained by both the thermodynamic factor (interfacial tension and spreading coefficient) and the kinetic factor (viscosity ratio). By adjusting the loading of PP and SEBS-g-MA, the core-shell particles with suitable size could be obtained, and the notched impact strength of the PA6 blends could be significantly improved. The effects of the loading of PP and SEBS-g-MA on tensile properties were also studied. Consequently, PA6 blends with high tensile strength and excellent impact strength could be obtained by loading only a small amount of SEBS-g-MA.
Core-Shell Particles Of Poly(Methyl Methacrylate)-Block-Poly(N-Butyl Acrylate) Synthesized Via Reversible Addition-Fragmentation Chain-Transfer Emulsion Polymerization And The Polymer'S Application In Toughening Polycarbonate

yue zhu,xiang gao,yingwu luo

DOI: https://doi.org/10.1002/app.42833

IF: 3

2016-01-01

Journal of Applied Polymer Science

Abstract:Poly(methyl methacrylate) (PMMA) block copolymer is interesting because it is compatible with many polymers. A series of poly(methyl methacrylate)-b-poly(n-butyl acrylate) (PMMA-b-PnBA) diblock copolymers with various compositions was synthesized via reversible addition-fragmentation chain-transfer (RAFT) emulsion polymerization with the amphiphilic oligo(methacrylic acid(41)-b-methyl methacrylate(8)) RAFT agent as both the polymerization mediator and surfactant. The molecular weights of the block copolymers agreed well with the theoretical prediction, although the polydispersity indices were relatively broad. The resulting core [poly(n-butyl acrylate)]-shell (PMMA) particles of PMMA-b-PnBA were found to be very effective impact modifiers for polycarbonate (PC). The diblock copolymer was well dispersed in 100-300-nm particles in the PC matrix, and the dispersed particle size was highly dependent on the block copolymer compositions. PMMA(250)-b-PnBA(550) (the subscripted number signifies the designed degree of polymerization), which was dispersed into 100-nm particles, presented the best capability for improving the impacting properties. Compared with the neat PC, the notched impact strength of PC toughened by 5 wt % PMMA(250)-b-PnBA(550) was increased by four times to 62.81 kJ/m(2) with the same yield strength, a slightly decreased modulus, an increased elongation at break, and an increased tensile strength. (c) 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 132, 42833.
Toughening of Pbt/Pc Blends with Epoxy Functionalized Core-Shell Modifiers

Fangfang Zhang,Shulin Sun,Xiaoyun Liu,Lixia Zhang,Huixuan Zhang

DOI: https://doi.org/10.1515/epoly.2009.9.1.939

2009-01-01

e-Polymers

Abstract:Core-shell modifiers of MB-g-GMA have been synthesized by emulsion polymerization technique. For these modifiers, the core is made up of the crosslinked poly(butadiene) and the shell is methyl methacrylate (MMA) and glycidyl methacrylate (GMA) copolymer. These modifiers were used to toughen poly(butylene terephthalate) (PBT)/bisphenol A polycarbonate (PC) blends. The mechanical properties showed that the addition of 15% MB-g-GMA had a very good influence on the notched Izod impact strength and elongation at break of the PBT/PC blends. DMA results showed PBT was partially miscible with PC and the addition of MB-g-GMA further improved the miscibility of PBT and PC. DSC tests further testified the introduction of MB-g-GMA improved miscibility between PBT and PC. Scanning electron microscopy (SEM) displayed a very good dispersion of MB-g-GMA particles in PBT/PC blend. Transmission electron microscopy (TEM) proved MB-g-GMA particles were enveloped by a thin layer of PC, PBT and PC showed co-continuous structure or dispersed phase which depended on the content of MB-g-GMA. SEM results showed shear yielding of the matrix and cavitation of rubber particles were the major toughening mechanisms.
Inhibited Transesterification on the Properties of Reactive Core-Shell Particles Toughened Poly(Butylene Terephthalate) and Polycarbonate Blends

Tingting Wen,Yang Guo,Shixin Song,Shulin Sun,Huixuan Zhang

DOI: https://doi.org/10.1007/s10965-015-0869-1

IF: 3.061

2015-01-01

Journal of Polymer Research

Abstract:Reactive core-shell particles with polybutadiene as core (297 nm) and methyl methacrylate-co-styrene-co-glycidyl methacrylate terpolymer as shell (PB-g-MSG) were prepared to toughen poly(butylene terephthalate) (PBT) and polycarbonate (PC) blends. Sodium pyrophosphate (SPP) was used to modify the transesterification between PBT and PC. FTIR results proved the occurrence of the transesterification and the addition of SPP inhibited the exchange reactions. SEM displayed the PB-g-MSG particles dispersed in PBT/PC matrix uniformly and the addition of SPP had no negative influence on the uniform dispersion. The crystallization temperature of PBT increased with the addition of SPP which indicated the constraint of PC block on the crystallization of PBT chain became poor. At the same time, with the addition of SPP into the PBT/PC/PB-g-MSG blend, the T-g of PC phase further shifted to higher temperature. PB-g-MSG was an effective toughener for PBT/PC blends, however, SPP decreased the toughening efficiency of PB-g-MSG particles for the PBT/PC blends. The yield strength and tensile modulus of PBT/PC blends increased first and then deceased with the increase of SPP content in the blends. Fracture mechanisms results showed the addition of SPP was not beneficial to the cavitation of the core-shell particles and shear yielding of the matrix and led to the decreased impact toughness.
Effect of PBT Resin on the Structure and Properties of Core-Shell Particles Toughened PC

Xingyue Wang,Shulin Sun,Deyin Zou,Zhongyao Zhao,Junjie Ma

2012-01-01

Abstract:Methyl methacrylate-butadiene-styrene-glycidyl methacrylate(MBS-g-GMA) core-shell particles were prepared to toughen polycarbonate(PC).The addition of poly(butylene terephthalate)(PBT) into the blends improves the dispersion of PC/MBS-g-GMA and MBS-g-GMA in PC matrix.The notched impact strength of the blends is improved,and when the mass fraction of PBT is 20%,impact strength of 700J/m can be achieved.The melt flow rate of PC/MBS-g-GMA blends increases with the introduction of PBT and the processability is improved.The fracture morphology shows the size of stress-whitening zone increases due to the addition of PBT and the shear yielding becomes much obvious and the toughness of the blends is improved.
Modification of Reactive PB‐g‐SAG Core–shell Particles to Achieve Higher Toughening Ability for Brittle Polylactide

Chunbo Hao,Shusong Zheng,Shulin Sun

DOI: https://doi.org/10.1002/pen.26008

2022-01-01

Abstract:Core-shell structured particles have been used to toughen brittle polylactide (PLA) extensively. In this research, reactive core-shell (RCS) particles with polybutadiene (PB) as core and the terpolymer styrene-acrylonitrile-glycidyl methacrylate as shell were prepared to improve the toughening ability of RCS for PLA. The tert-dodecyl mercaptan (TDDM) content was varied during polymerization and higher TDDM concentrations induced lower grafting and cross-linking of the PB phase, which significantly influenced the dispersed phase morphology and toughness of RCS toughened PLA blends. With the increase of TDDM content, the phase morphology of RCS changed from uniform dispersion, net-like structure to an agglomeration pattern. The impact strength of PLA blends increased with TDDM content and reached 922 J/m for the PLA/RCS-T5 (TDDM: 1.18 wt%), which was 30 times higher than pristine PLA and similar to 3 times than PLA/RCS-T0 blend. Higher TDDM contents decreased toughening efficiency. Appropriate TDDM contents decreased the glass transition temperature (T-g) and cross-linking degree of RCS particles which enhanced the cavitation ability of the PB core phase and promoted the shear yielding of PLA matrix. The modification effect of TDDM solves the problem of insufficient toughening ability of core-shell particles. Under the same toughener content, the modified RCS particles make the PLA blend achieve super toughness.
Relationship between structure and properties in high-performance PA6/SEBS-g-MA/(PPO/PS) blends: The role of PPO and PS

Yijian Wu,Hui Zhang,Baoqing Shentu,Zhixue Weng

DOI: https://doi.org/10.1002/app.45281

IF: 3

2017-01-01

Journal of Applied Polymer Science

Abstract:This work aimed at studying the role of poly(phenylene oxide) (PPO) and polystyrene (PS) in toughening polyamide-6 (PA6)/styrene-ethylene-butadiene-styrene block copolymer grafted with maleic anhydride (SEBS-g-MA) blends. The effects of weight ratio and content of PPO/PS on the morphology and mechanical behaviors of PA6/SEBS-g-MA/(PPO/PS) blends were studied by scanning electron microscope and mechanical tests. Driving by the interfacial tension and the spreading coefficient, the core-shell particles formed by PPO/PS (core) and SEBS-g-MA (shell) played the key role in toughening the PA6 blends. As PS improved the distribution of the core-shell particles due to its low viscosity, and PPO guaranteed the entanglement density of the PPO/PS phase, the 3/1 weight ratio of PPO/PS supplied the blends optimal mechanical properties. Within certain range, the increased content of PPO/PS could supply more efficient toughening particles and bring better mechanical properties. Thus, by adjusting the weight ratio and content of PPO and PS, the PA6/SEBS-g-MA/(PPO/PS) blends with excellent impact strength, high tensile strength, and good heat deflection temperature were obtained. (c) 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 45281.
Effectively toughening polypropylene with in situ formation of core-shell starch-based particles

Guangxin Wang,Song Li,Yulin Feng,Yuexin Hu,Guiyan Zhao,Wei Jiang

DOI: https://doi.org/10.1016/j.carbpol.2020.116795

IF: 10.723

2020-12-01

Carbohydrate Polymers

Abstract:Impact modifier particles with the core-shell structure in the polypropylene (PP) matrix were successfully prepared in situ by melt blending PP, thermoplastic starch acetate (TPAS) and poly(ethylene octane) grafted with maleic anhydride (POE-MA). It was found that the core was formed by TPAS, while the shell was formed by POE-MA. This core-shell particle plays an important role in toughening PP. The notched impact strength of PP/TPAS/POE-MA blend was as high as 68.1 KJ/m2 with an anticipated cost effectiveness. The mechanism of formation of the core-shell starch-based particles could be ascribed to the reactive compatibilization between TPAS and POE-MA which could be confirmed by SEM, and which dramatically improved the mechanical properties of the composites. This provides a new idea for the toughening modification of nonpolar PP, which could widely extend the application of starch and lower the cost.

polymer science,chemistry, organic, applied
Synergistic Effect of Polycarbonate on Reactive Core-Shell Particles Toughened Poly (butylene Terephthalate)

Yang Guo,Jinxin He,Xina Zhang,Shulin Sun,Huixuan Zhang

DOI: https://doi.org/10.1080/00222348.2015.1020258

2015-01-01

Abstract:Glycidyl methacrylate functionalized methyl methacrylate-butadiene-styrene copolymer (MBS-g-GMA) core-shell particles were prepared via an emulsion polymerization process. MBS-g-GMA was used to toughen poly(butylene terephthalate) (PBT) and the synergistic toughening effect of polycarbonate (PC) on PBT/MBS-g-GMA blends were investigated. Notched impact tests showed the percolation threshold became lower with the increase of PC content. Transmission electron microscopy displayed a very good dispersion of MBS-g-GMA particles in the PBT matrix with the different PC contents. The synergistic toughening effect was due to the encapsulation structure of PC which could facilitate the whole PBT matrix to yield. The more perfect the encapsulation structure formed, the more obvious the synergistic toughening the PC achieved. Sufficient strength of the phase interface was important to ensure the stress transfer effectively and facilitate the whole PBT matrix to yield. The interface strength between PC and MBS-g-GMA could be ensured by the good miscibility between Poly(methyl methacrylate) (PMMA) (grafted onto the polybutadiene-based rubber core) and PC. For the PBT/PC, the transesterification between PBT and PC improved the interface strength of the PBT and PC phases, as demonstrated by Fourier transform infrared spectroscopy (FTIR) scans. Scanning electron microscopy results showed shear yielding of the matrix and cavitation of the rubber particles were the major toughening mechanisms.
Fabrication and toughening mechanism of high toughness PP/SEBS/HDPE blends with core‐shell particles

Shushu Li,Pengfei Cheng,Xiaoyan Liu,Guangquan Li,Yingxia Ma

DOI: https://doi.org/10.1002/pol.20230234

IF: 3.046

2023-07-21

Journal of Polymer Science

Abstract:Aiming at obtaining high toughness polypropylene (PP) products, in this work, using high density polyethylene (HDPE) and styrene‐ethylene‐butylene‐stryrene (SEBS) as toughening agents, PP/SEBS/HDPE blends were successfully fabricated by melt‐blending method, and the microstructure, mechanical, thermodynamics, and rheological properties of the blends were investigated. The results revealed the core‐shell structure particles with HDPE as the core and SEBS as the shell were dispersed in PP in the PP/SEBS/HDPE blends. The core‐shell structure particles played good roles in toughening PP matrix, and the PP/SEBS/HDPE blends underwent brittle‐tough transition at 15 wt% SEBS and 5 wt% HDPE. The impact toughness of PP/SEBS/HDPE blends with 15 wt% SEBS and 15 wt% HDPE reached 60.1 kJ/m2, which was almost 1441.0% that of pure PP. The formation of core‐shell particles in the system led to an increase in the degree of chain entanglement between the dispersed phase and PP, which enhanced the interfacial adhesion. In addition, based on the experimental results, the relationship between the viscosity and the material toughness was proposed, revealing the brittle‐ductile transition behavior and the toughening mechanism.

polymer science
Preparation of PP toughening masterbatch with core-shell structure

Yang Junzhong,Jing Zhenhua,Liu Wei,Wang Yanwei

DOI: https://doi.org/10.3969/j.issn.1002-1396.2006.01.002

2006-01-01

Abstract:A kind of polypropylene (PP) toughening masterbatch was developed with taking graft of maleic anhydride as modifier. The micro-structure, crystallinity and rheology of the masterbatch were characterized by scanning electron microscopy, transmission electron microscopy, differential scanning calorimetry and Fourier transform infrared spectroscopy. The results reveal that the toughening masterbatch possesses typical core-shell structure. In the case of adding 10% of the toughening masterbatch, the impact strength of the propylene homopolymer can be increased by 1 fold compared with its counterpart containing the same quantity of the traditional toughening modifier. In addition, the bending modulus of the propylene homopolymer is raised by 20%.
Preparation and Properties of PMMA Blends with High Toughness

Shu-wen ZHANG,Yue TAO,Wei-ge TANG,Gui-ping YUAN,Wen-tao LIU,Shu-lin SUN

DOI: https://doi.org/10.3969/j.issn.1005-5770.2017.04.008

2017-01-01

Abstract:Poly(methyl methacrylate)/polybutadiene grafting copolymer(PB-g-PMMA) was prepared by the emulsion polymerization method and the PB-g-PMMA particles were used to toughen poly (methyl methacrylate) (PMMA) resin.Poly (vinylidene fluoride) (PVDF) was introduced into the blends to improve the toughness synergistically.The toughening behavior of the blends was investigated.The results show that the glass transition temperature of PMMA shifts to lower temperature with the addition of PVDF.PMMA and PVDF display good miscibility.PB-g-PMMA particles disperse in PMMA matrix uniformly and the addition of PVDF does not affect the dispersion of PB-g-PMMA particles.The impact strength of PMMA/PB-g-PMMA is 30 J/m.When the content of PVDF is 40％,the impact strength of the blend is 305 J/m.PVDF improves the toughening efficiency of PB-g-PMMA.Fracture results indicate that shear yielding will take place when the content of PVDF is more than 20％.So the toughness of the blends is improved significantly.
Effect of Core-shell Ratio of the Modifier on the Properties of Toughened Polylactide Acid

Wen-tao LIU,Yun-xia L(U),Jing-yu CHEN,Shu-wen ZHANG,Shu-lin SUN

DOI: https://doi.org/10.3969/j.issn.1005-5770.2017.07.008

2017-01-01

Abstract:The reactive core-shell (RCS) particles with methyl methacrylate-styrene-glycidyl methacrylate copolymer as shell and polybutadiene as core were prepared by the emulsion polymerization method.The influence of the ratio of core to shell for the RCS particles on the toughening properties of polylactide acid(PLA) was investigated.The grafting degree and particle size of the RCS particles decrease with the increase of the core/shell ratio.Scanning electron microscope observation indicated that the RCS particles dispersed in the PLA matrix uniformly.Dynamic mechanical analysis results showed the glass transition temperature of the shell phase shifted to lower temperature with the increase of core-shell ratio,meaning the good miscibility between PLA and the RCS particles.The toughness improves with the increase of core-shell ratio.When the core-shell ratio was higher than 50/50,the impact strength of 630 J/m was achieved for the PLA blends and the yielding strength of the PLA blends decreased.
The compatibilization of poly (propylene carbonate)/poly (lactic acid) blends in presence of core-shell starch nanoparticles

Xinyi Dong,Li Liu,Yang Wang,Ting Li,Zhenggui Wu,Hao Yuan,Piming Ma,Dongjian Shi,Mingqing Chen,Weifu Dong

DOI: https://doi.org/10.1016/j.carbpol.2020.117321

IF: 10.723

2021-02-01

Carbohydrate Polymers

Abstract:A novel core-shell starch-based nanoparticles (CSS NPs) with a "hard" starch core and a "soft" poly (methyl acrylate) (PMA) shell was prepared and incorporated into a PPC/PLA blend. The excellent compatibilization of CSS NPs was revealed by atomic force microscope (AFM), differential scanning calorimetry (DSC) and rheological test. More importantly, due to the excellent compatibilization the resulted PPC/PLA/CSS blend exhibited a strikingly improved mechanical and thermal properties. Compared to PPC/PLA (60/40), the elongation at break of PPC/PLA/CSS (60/40/20) increased greatly from 15 % to 272 % without sacrificing the tensile strength. Besides, the heat distortion temperature (HDT) of PPC/PLA/CSS (60/40/20) was improved to 47.3 °C, which was 20.5 °C higher than that of the neat PPC. These results established a novel and efficient strategy to improve the compatibility of polymer blends and to prepare polymer blends with balanced toughness and stiffness.

polymer science,chemistry, organic, applied
Construction of Core‐Shell Structure in PA6/ABS/SEBS Blends for Achieving Stiffness‐Toughness Balance

Sibo Cheng,Tiantian Li,Mingzhe Jiang,Jintang Duan,Lianfang Feng,Xueping Gu,Cailiang Zhang

DOI: https://doi.org/10.1002/adem.202402110

IF: 3.6

2024-01-01

Advanced Engineering Materials

Abstract:A mixed system of styrene‐ethylene‐butene‐styrene copolymer (SEBS) and acrylonitrile‐butadiene‐styrene copolymer (ABS) is used to modify polyamide 6 (PA6). The incorporation of maleic anhydride‐grafted SEBS (SEBS‐g‐MAH) facilitates a reaction between the anhydride functional groups and the terminal amine group of PA6, resulting in SEBS predominantly localizing at the interface between PA6 and ABS. This leads to the formation of core‐shell structure particles within the PA6 matrix, where ABS forms the hard core and SEBS constitutes the soft shell. As the content of SEBS‐g‐MAH increases, the thickness of SEBS shell grows, enhancing the impact strength of PA6/ABS (70/15) by 3.5 times at 30 parts of SEBS‐g‐MAH. The introduction of MAH‐grafted ABS as a compatibilizer in the PA6/ABS/SEBS‐g‐MAH (60/30/10) system significantly reduces the size of core‐shell particles, yielding a 3.4‐fold increase in impact strength and a simultaneous twofold increase in tensile strength at 10 parts of ABS‐g‐MAH. This dual enhancement provides an optimal balance between rigidity and toughness.
Preparation and Properties of Core-Shell Particles Filled Β-Nucleated Polypropylene Random Copolymer Composites

Youchen Li,Guixin Zhang,Xiaowei Fu,Weihong Guo

DOI: https://doi.org/10.1177/096739111502300101

2015-01-01

Polymers and Polymer Composites

Abstract:To provide polypropylene random copolymer (PPR) with excellent toughness without lowering its rigidity, a novel kind of core-shell particles (CSP) and β nucleating agent (β-NA) were incorporated into PPR by melt blending. The CSP, in which nano-CaCO3 acted as the core and polyethylene (PE) formed the shell, was also prepared through melt blending. The effects of different proportion of PE shell and nano-CaCO3 core on the properties of β-modified PPR composites were investigated. The dispersion and morphology of CSP were studied by transmission electron microscopy (TEM) and the results showed that the CSP dispersed fairly well in the PPR matrix and the core-shell structure was successfully formed. The nano-CaCO3 core was completely encapsulated by PE, especially at the 50/50 weight ratio. The crystallization behaviour of the PPR composites was characterized by differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WAXD) and polarized optical microscopy (POM). All the results showed that the relative content of β-form crystal was greatly enhanced with the incorporation of β-NA. Furthermore, the weight ratio change of PE/nano-CaCO3 could also increase the relative content of the β-form crystal. Under the combined effects of β-modification and CSP, the mechanical properties of the PPR composites were greatly enhanced without reducing its rigidity.

Modification of the Core–shell Ratio to Prepare PB-g-(MMA-co-St-co-GMA) Particle-Toughened Poly(butylene Terephthalate) and Polycarbonate Blends with Balanced Stiffness and Toughness

Preparation of PBT/POE‐g‐GMA/PP Ternary Blends with Good Rigidity–toughness Balance by Core–shell Particles

Modification of the Reactive Core-Shell Particles Properties to Prepare PBT/PC Blends with Higher Toughness and Stiffness

PREPARATION AND CHARACTERISTICS OF PBA/PMMA CORE-SHELL PARTICLES AS TOUGHER

Effect of Core-Shell Particles Dispersed Morphology on the Toughening Behavior of PBT/PC Blends

In Situ Formation of the Core–Shell Particles and Their Function in Toughening PA6/SEBS-g-MA/PP Blends

Core-Shell Particles Of Poly(Methyl Methacrylate)-Block-Poly(N-Butyl Acrylate) Synthesized Via Reversible Addition-Fragmentation Chain-Transfer Emulsion Polymerization And The Polymer'S Application In Toughening Polycarbonate

Toughening of Pbt/Pc Blends with Epoxy Functionalized Core-Shell Modifiers

Inhibited Transesterification on the Properties of Reactive Core-Shell Particles Toughened Poly(Butylene Terephthalate) and Polycarbonate Blends

Effect of PBT Resin on the Structure and Properties of Core-Shell Particles Toughened PC

Modification of Reactive PB‐g‐SAG Core–shell Particles to Achieve Higher Toughening Ability for Brittle Polylactide

Relationship between structure and properties in high-performance PA6/SEBS-g-MA/(PPO/PS) blends: The role of PPO and PS

Effectively toughening polypropylene with in situ formation of core-shell starch-based particles

Synergistic Effect of Polycarbonate on Reactive Core-Shell Particles Toughened Poly (butylene Terephthalate)

Fabrication and toughening mechanism of high toughness PP/SEBS/HDPE blends with core‐shell particles

Preparation of PP toughening masterbatch with core-shell structure

Preparation and Properties of PMMA Blends with High Toughness

Effect of Core-shell Ratio of the Modifier on the Properties of Toughened Polylactide Acid

The compatibilization of poly (propylene carbonate)/poly (lactic acid) blends in presence of core-shell starch nanoparticles

Construction of Core‐Shell Structure in PA6/ABS/SEBS Blends for Achieving Stiffness‐Toughness Balance

Preparation and Properties of Core-Shell Particles Filled Β-Nucleated Polypropylene Random Copolymer Composites