Abstract:A series of mesostructured Cu-SiO2 composites have been synthesized with sodium metasilicate (Na2SiO3) and cuprammonia nitrate (Cu(NH3)(4)(NO3)(2)) respectively used as Si and Cu sources. The synthetic procedures were conducted at room temperature, and cetyltrimethylammonia bromide was used as a template. Under our experimental conditions, ordered mesoporous Cu-SiO2 composites could be obtained with a copper content up to 16.8 wt %. Average pore diameters (2.80-3.15 nm), wall thickness (1.30-2.20 nm), and specific surface area (1020-690 m(2)/g) are found to vary linearly with copper content (0-16.8 wt %). Results of thermal gravimetry-differential thermal analysis reveal the collapse temperature of the order structure starts at similar to1250 K for mesoporous Cu-SiO2 with 16.8 wt % copper content. As indicated by the outcomes of inductively coupled plasma and X-ray photoelectron spectroscopy studies, copper is mainly incorporated inside the pore wall rather than embedded on the wall surface. Copper species strongly interact with silica, and calcination at high temperatures cannot cause phase separation between silica and copper oxide. Cu status in mesoporous Cu-SiO2 composites is similar to that in copper silicate in neighboring structures. Based on the results, a S+I-I+I- mechanism is proposed in which copper entities are surrounded by silicon species during synthesis of the mesostructured composite.

Study on the Synthesis and Structure of Cu-Zsm-5 Type Molecular Sieve

The Preparation of ZSM-5 Zeolite@cu/stainless Steel As a Dual Functional Material

Synthesis and characterization of MCM-49/ZSM-35 composite zeolites in the hexamethyleneimine and cyclohexamine system

Synthesis and characterization of titanium silicate molecular sieves with zorite-type structure

SYNTHESIS OF MESOPOROUS MOLECULAR SIEVES WITH SECONDARY BUILDING UNITS OF β ZEOLITE AT LOW SURFACTANT CONCENTRATION

Structures of highly siliceous ZSM-5 zeolites and Ti- ZSM-5 zeolites obtained by indirect synthesis

Ionothermal Synthesis of Hierarchical Structured CuAPO-5 Molecular Sieve

Synthesis and structure characterization of mesoporous zinc silicate/silica composites

Enhanced CO2 Adsorption Performance on Hierarchical Porous ZSM-5 Zeolite

Influence of cations (Li+, Na+, K+)for synthesis mesoporous molecular sieve MCM-41 and their properties

Structure of Highly Siliceous ZSM-5 Zeolites and Ti-ZSM-5 Zeolites Obtained by Indirect Synthesis

Synthesis of ZSM-5 Zeolite Using Γ-Aminopropyl Triethoxylsilane As Structure-directing Agents

Synthesis of Mesoporous Zsm-5 Zeolite Crystals by A New Organosilane Template with Double-Oxycarbonyl Carbon Chains

Synthesis of Mesoporous Molecular Sieves with Secondary Building Units of Y Zeolite by Using Surfactants in Low Concentration as Template

Preparation of ZSM-5 molecular sieve modified by kaolin and its CO2 adsorption performance investigation

SYNTHESIS AND CHARACTERIZATION OF NANOSIZED Mo-ZSM-5 ZEOLITE

Synthesis of nanosized MFI zeolites using Cu-containing complexes

A Mesoporous ZSM-5 Zeolite Synthetized by a Novel Double Long-Alkyl-Chain Organosilane Template

Shape-controlled Synthesis of Monolithic ZSM-5 Zeolite with Hierarchical Structure and Mechanical Stability

Novel coassembly route to Cu-SiO2 MCM-41-like mesoporous materials.

Synthesis and Characterization of Mesoporous Zirconia Molecular Sieve