Microstructure and Hardness of Mg-8Zn-2Si-0.5Ca Alloy Before and After Heat Treatment

赵红亮,石广新,郑飞燕,张春香,周占霞,关绍康

DOI: https://doi.org/10.3969/j.issn.1001-3814.2004.12.021

2004-01-01

Abstract:Microstructure and hardness of Mg-8Zn-2Si-0.5Ca alloy after heat treatment were investigated. The results show that the alloy is comprised of α-Mg,MgZn,Mg_2Si and CaSi_2 phase;the Mg_2Si appear as blocks and the particles are tinny; CaSi_2 phase is as the core of the Mg_2Si grains; after the solid solution treatment, the skeletal MgZn phase decreases clearly and its size becomes small;the solid solution treatment can′t make the Mg_2Si phase dissolve into the α-Mg matrix; the dissolved MgZn phase during the solid solution treatment precipitates tinny and dispersed phase after aging;after the solid solution treatment and aging, the hardness increases greatly.