Abstract:Ni-based catalysts dispersed on different supports (MgO-α-AlO, CeO, SBA-15, and MgO-SBA-15) were prepared by the impregnation method. Characteristics of the catalysts, including specific surface areas (N physisorption), crystalline phase compositions (powder X-ray diffraction, Raman spectroscopy), reducibility (hydrogen temperature-programmed reduction, H-TPR), and morphology (scanning electron microscopy (SEM) and transmission electron microscopy, TEM)) were investigated. The activity and stability of the catalysts were tested for the combined steam and CO reforming of methane at 700 °C in a microflow system. The results show that the catalysts exhibit high activity in the BRM reaction. At 700 °C, the conversion of CH and CO reached 86-99% and 67-80%, respectively, in which the Ni/Mg-SBA catalyst is the best with conversions of CH and CO reaching 99% and 80%. Coke accumulation on the surface of the catalysts for 100 h time on stream (TOS) was evaluated by the temperature-programmed oxidation (TPO) technique. The major cause of the catalytic deactivation was elucidated by combining the determination of the amount and type of deposited coke with the changes in the physicochemical properties of the catalysts after the long-term reaction. Almost complete loss of activity was observed on Ni/Mg-Al catalyst after 100 h TOS, while the activity drop was slow on the Ni/Mg-SBA sample, about 15-20% of the total value. Otherwise, the Ni/CeO and Ni/SBA catalysts firmly retained their stable activity for 100 h TOS due to the minimal carbon deposition and stability of these catalysts' structure. The highly considerable formation of inert C carbon and sintering over Ni catalyst supported on MgO-α-AlO were responsible for the lower stability of this catalyst compared to those supported on CeO and SBA-15.

Improved Catalytic Performance of Ni Catalysts for Steam Methane Reforming in a Micro-Channel Reactor

Steam reforming of methane over Ni catalyst in micro-channel reactor

An Innovative Micro-Channel Catalyst Support with a Micro-Porous Surface for Hydrogen Production Via Methanol Steam Reforming

Catalytic Performance of Ni Catalyst for Steam Methane Reforming in a Micro-Channel Reactor at High Pressure

Catalytic performance of Ni catalysts for steam reforming of methane at high space velocity

A comparative study of Rh and Ni coated microchannel reactor for steam methane reforming using CFD with detailed chemistry

Total methanation of syngas to synthetic natural gas over Ni catalyst in a micro-channel reactor

Balancing Ni0 and Ni2+ on Γ‐al2o3 for Efficient Steam Methane Reforming

Modulating Oxidation State of Ni/CeO2 Catalyst for Steam Methane Reforming: a Theoretical Prediction with Experimental Verification

Bi-reforming of Methane with Carbon Dioxide and Steam on Nickel-Supported Binary Mg–Al Metal Oxide Catalysts

Rapid fabrication of Ni supported MgO-ZrO 2 catalysts via solution combustion synthesis for steam reforming of methane for hydrogen production

Modulating Proportion of Ni0 Species Stabilized by Ni2+ on Ni-MgO Catalyst with Superior Stability for Dry Reforming of Methane

A Study on CO2 Methanation and Steam Methane Reforming over Commercial Ni/Calcium Aluminate Catalysts

Recent advances in promoting dry reforming of methane of Nickel-based catalysts

Ni-based bimetallic catalysts for hydrogen production via (sorption-enhanced) steam methane reforming

Ni/x%Nb2O5/Al2O3 Catalysts Prepared via Coprecipitation-Wet Impregnation Method for Methane Steam Reforming

Effect of Support on Stability and Coke Resistance of Ni-Based Catalyst in Combined Steam and CO Reforming of CH.

Methane steam reforming for hydrogen production using low water-ratios without carbon formation over ceria coated Ni catalysts

Highly dispersed Ni/MgO-mSiO2 catalysts with excellent activity and stability for dry reforming of methane

Modification of a micro-mesoporous Ni/ZSM-5 catalyst for steam reforming of toluene

Evaluation of promoted Ni-based nanocatalysts in wall-coated microchannel reactor on the dry reforming of methane and effect of ultrasound waves on physiochemical properties of synthesized nanocatalysts