Abstract:This paper presents a numerical study of creep crack growth (CCG) in a fracture mechanics specimen. The material properties used are representative of a carbon–manganese steel at 360 °C and the constitutive behaviour of the steel is described by a power law creep model. A damage-based approach is used to predict the crack propagation rate in a compact tension specimen and the data are correlated against an independently determined C∗ parameter. Elastic–creep and elastic–plastic–creep analyses are performed using two different crack growth criteria to predict crack extension under plane stress and plane strain conditions. The plane strain crack growth rate predicted from the numerical analysis is found to be less conservative than the plane strain upper bound of an existing ductility exhaustion model, for values of C∗ within the limits of the present CCG testing standards. At low values of C∗ the predicted plane stress and plane strain crack growth rates differ by a factor between 5 and 30 depending on the creep ductility of the material. However, at higher loads and C∗ values, the plane strain crack growth rates, predicted using an elastic–plastic–creep material response, approach those for plane stress. These results are consistent with experimental data for the material and suggest that purely elastic–creep modelling is unrealistic for the carbon–manganese steel as plastic strains are significant at relevant loading levels.

Application of Small Crack Growth Law to Different Types of Loading.

Evaluation Method of Fatigue Crack Growth Rates at Various Stress Rations. Investigation Based on Small Crack Growth Law.

Validity of Small-Crack Growth Law for Large Cracks.

Prediction of Fatigue Life Based on Small Crack Growth Law.

Unified Evaluation of Fatigue Crack Growth Rates under Rotating Bending and Plane Bending.

Instrumented indentation measurements of residual stresses around a crack tip under single tensile overloads

Effect of Specimen Configuration and Loading Types on Fatigue Life of an Annealed 0.42% Carbon Steels

Fatigue crack growth in degrading elastic components of nonlinear structural systems under random loading

Effect of Cross-Sectional Shape of Specimen on Fatigue Strength under Plane Bending.

Evaluation Of Excessive Loading Effect On Fatigue Crack Growth Behavior Based On Crack Blunting And Stress Distribution In Front Of The Crack Tip

EVALUATION OF SMALL CRACK GROWTH RATE OF ALUMINUM ALLOYS UNDER DIFFERENT STRESS GRADIENTS

Short Fatigue-Crack Growth from Crack-like Defects under Completely Reversed Loading Predicted Based on Cyclic R-Curve

Investigation on Evaluation Method Based on J Integral for Retardation of Crack Growth Due to Excessive Loading Beyond Small Scale Yielding Condition

OS0807 Evaluation of Crack Growth under Seismic Loading in Nickel Based Alloy Weld

Small Crack Growth Behavior And Life Prediction Of 7075-T73 Forged Aluminum Alloy

STUDY OF FATIGUE CRACK GROWTH RETARDATION, CRACK TIP DEFORMATION AND CRACK CLOSURE UNDER SINGLE OVERLOAD APPLICATION FOR A537 STEEL

Statistical Analysis Methods of Fatigue Crack Growth Rate

In-situ observation of strain evolution and ratchetting of growing fatigue cracks

OS0503 Effect of Excessive Compressive Loading on the Crack Growth Behavior

Simple Predicting Method for Fatigue Crack Growth Rate Based on Tensile Strength of Carbon Steel

Creep crack growth prediction using a damage based approach