Abstract:This paper deals with the results of the low cycle fatigue tests on hour-glass type and round notched specimens of SM 41 A. Strain-controlled and load-controlled low cycle fatigue tests at ambient temperature were carried out to investigate the notch effect on the fatigue strength reduction factor.The following conclusions were obtained :1) A visible crack of 0.2 to 0. 5 mm in length will be initiated on the notch root of a notched specimen with any shape factor at an approximately same number of cycles, if the same equivalent strain at the root of a notch is used as the measure of evaluating strain amplitude.2) A concept was proposed on low cycle fatigue strength reduction factor. The fatigue strength reduction factor Kf, _??_ which is calculated from the results of strain-controlled low cycle fatigue tests on smooth and notched specimens, would be equal to the dynamic strain concentration factor. In case that no low cycle fatigue tests would be carried out, the fatigue strength reduction factor may be obtained from the result of dynamic strain analysis.3) “A” factor for a carbon steel, which is given in the Fig. D-201 in the Nuclear Piping Code (USAS B 31. 7 1969), is found to give lower and higher value than the Kf, _??_ value depending on an applied stress amplitude. It is also revealed that “A” factor in the Nuclear Power Piping Code is much lower than that obtained by the Method proposed by S. W. Tagart for the material used in the present test.

Effect of Cross-Sectional Shape of Specimen on Fatigue Strength under Plane Bending.

Unified Evaluation of Fatigue Crack Growth Rates under Rotating Bending and Plane Bending.

Effect of Specimen Configuration and Loading Types on Fatigue Life of an Annealed 0.42% Carbon Steels

Evaluation Method of Fatigue Crack Growth Rates at Various Stress Rations. Investigation Based on Small Crack Growth Law.

Application of Small Crack Growth Law to Different Types of Loading.

Effect of Pre-Strain on Fatigue Strength of Aluminum Alloy 5052.

Size Effect on the Fatigue Performance of 18CrNiMo7‐6 Alloy Steel

Simple Predicting Method for Fatigue Crack Growth Rate Based on Tensile Strength of Carbon Steel

Effect of Bending-Torsion on Fracture and Fatigue Life for 18ni300 Steel Specimens Produced by SLM

The Fatigue Life Prediction Method of Notched Specimen Based on the Critical Plane

Influence of Loading Path on Fatigue Crack Growth under Multiaxial Loading Condition

Effect of a New Specimen Size on Fatigue Crack Growth Behavior in Thick-Walled Pressure Vessels

Prediction of Bending Fatigue Life of Cracked Out-of-Plane Gusset Joint Repaired by CFRP Plates

Effect of Specimen Thickness and Stress Intensity Factor Range on Plasticity-Induced Fatigue Crack Closure in A7075-T6 Alloy

Low Cycle Fatigue Strength Reduction Factor for a Mild Steel

Extremely Low-Cycle Fatigue Tests of Thick-Walled Steel Bridge Piers

Prediction of Fatigue Life Based on Small Crack Growth Law.

Statistical Analysis Methods of Fatigue Crack Growth Rate

Effect of Residual Stress on Fatigue Behaviour of Notches

Probabilistic Control Volume Method for Evaluating the Effects of Notch Size and Loading Type on Fatigue Life