Abstract:The study mainly investigates the effect of strain ratio on the multiaxial low cycle fatigue behaviour of 316L at 550 °C. The evolution of both axial and torsional stress amplitude is observed to go through three stages: cyclic hardening, softening and fracture. What's different is that the torsional loading experiences fewer cyclic hardening cycles compared to the axial loading. Regarding the interaction between axial and torsional stresses, it is observed that as the torsional strain increases, the axial deformation response presents a lower peak stress and a higher softening rate, while the torsional peak stress and softening rate hardly changes with the increase of axial strain amplitude. The fracture pattern is obtained through three-dimensional (3D) depth-of-field observation. It is discovered that as the strain ratio increases, the fracture pattern transits from tensile failure mode to shear failure mode. Furthermore, the orientation angle of the fracture surface increases and lies between the critical plane angle of maximum shear strain and maximum normal strain, indicating a mixed failure mode. Additionally, a comparison of nine representative critical plane models reveals that the energy-based models can better predict the multiaxial fatigue life influenced by the strain ratio. Finally, based on the analysis of deformation and failure mechanisms, a normal damage parameter weakening factor (NDWF) is introduced into the KBM-R model, and an improved normal stress component (INSC) is introduced into the Wu-R model. The two modified models well capture the impact of strain ratio and accurately predict the multiaxial fatigue life of both 316L and P92 steel.

EFFECT OF CYCLIC STRESS-STRAIN BEHAVIOR ON THE PREDICTION OF FATIGUE LIFE FOR CARBON STEEL

Study on the Prediction Method of the Ultra-Low-Cycle Fatigue Damage of Steel

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

A New Empirical Life Prediction Model For 9-12%Cr Steels Under Low Cycle Fatigue And Creep Fatigue Interaction Loadings

Experimental and Numerical Characterization of Low Cycle Fatigue and Creep Fatigue Behaviour of P92 Steel Welded Joint

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Effect of Specimen Configuration and Loading Types on Fatigue Life of an Annealed 0.42% Carbon Steels

Modeling of Low Cycle Behavior of P92 Steel Based on Cyclic Plasticity Constitutive Equations

Simple Predicting Method for Fatigue Crack Growth Rate Based on Tensile Strength of Carbon Steel

Effective stress and fatigue life prediction with mean stress correction models on a ferritic stainless steel sheet

Assessment of prior fatigue damage and a new approach to predict remanent creep rupture of P92 steel

On multiaxial creep–fatigue considering the non-proportional loading effect: Constitutive modeling, deformation mechanism, and life prediction

A Simple Engineering Approach in the Prediction of the Effect of Stress Ratio on Fatigue Threshold

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

A Fatigue Life Prediction Approach for Resistance Spot Welded Joints with Consideration of the Stress Ratio Effect

An improved life prediction strategy at elevated temperature based on pure creep and fatigue data: Classical strain controlled and hybrid stress-strain controlled creep-fatigue test

Development of improved Manson-Coffin model considering the effect of yield stress under asymmetrical cyclic loading

Effect of stress ratios on corrosion fatigue life of high‐strength steel wires

The strain ratio-dependent multiaxial low cycle fatigue behaviour and life prediction of 316L stainless steel based on critical plane at elevated temperature

Multiaxial fatigue life prediction for metals by means of an improved strain energy density-based critical plane criterion