Effece of Cu3P on microstructure and mechanical properties of Fe-2Ni-1Cu-0.6C double pressed/double sintered materials

You-fu LI,Zhi-you LI,Hao TENG,Hai-Zu ZENG,Ke-chao ZHOU

DOI: https://doi.org/10.3969/j.issn.1673-0224.2015.01.007

2015-01-01

Abstract:Powder metallurgical Fe-2Ni-1Cu-0.6C alloy was prepared by double press/double sinter (DP/DS) processing. The effect of Cu3P additive on microstructure and mechanical properties of the iron-based alloy was investigated, as well as the optimizing of pre-sintering process was carried out by adjusting the pre-sintering temperature. The results show that: the bending strength and hardness of the Fe-2Ni-1Cu-0.6C double pressed/double sintered alloy are improved by adding minor Cu3P due to the sinter assisting, pearlite structure homogenizing and significant solution strengthening generated by phosphorus. Optimizing of pre-sintering temperature can reduce the losing of double-pressed density and impact toughness caused by the addition of Cu3P,which leads to a further increase of mechanical properties of the Cu3P contained alloys. The maximum values of bending strength and Rockwell hardness can be obtained in Fe-2Ni-0.5Cu-0.58Cu3P-0.6C alloy with pre-sintering temperature of 720℃are 1 354 MPa and 85.5 HRB, respectively, in addition, the impact energy of the alloy is 8.61J·cm?2.