Correlation between microstructure and soft magnetic parameters of Fe-Co-Ni-Al medium-entropy alloys with FCC phase and BCC phase
Xiaohua Tan,Yajie Tang,Yunfeng Tan,Qin Deng,Huisheng Jiao,Yang Yang,Hui Xu
DOI: https://doi.org/10.1016/j.intermet.2020.106898
IF: 4.075
2020-11-01
Intermetallics
Abstract:<p>The magnetic property and microstructure of as-cast FeCoNiAl<sub>x</sub> (x = 0.2, 0.4, 0.6, 0.8, 1.0) MEAs prepared by copper mold suction were investigated. For x ≤ 0.6 alloys, the soft magnetic properties monotonously decrease with increasing Al content, while a turning point of improving magnetic property occurs at x = 0.8. XRD result shows that Al addition changes the phase constitution. The alloys (x ≤ 0.4) consist of single FCC phase. FeCoNiAl<sub>0.6</sub> (x = 0.6) and FeCoNiAl<sub>0.8</sub> (x = 0.8) alloys are composed of FCC phase and BCC phase. FeCoNiAl<sub>1.0</sub> (x = 1.0) alloy consists of single BCC phase. Furthermore, more serious lattice distortion is present in FCC phase than that in BCC phase. It results in the deterioration of soft magnetic property by increasing the coercivity (H<sub>c</sub>) and the hysteresis loss (P<sub>u</sub>), and decreasing the initial permeability (μ<sub>i</sub>) and the maximum permeability (μ<sub>m</sub>). The grain-boundary character distribution of FeCoNiAl<sub>0.6</sub> (x = 0.6) alloy and FeCoNiAl<sub>0.8</sub> (x = 0.8) alloy was studied by electron backscatter diffraction (EBSD). Less strain concentration is observed in x = 0.8 alloy than that in x = 0.6 alloy because of containing much smaller number of low angle boundaries (LAB) with a misorientation angle between 2° and 5° (5.71%) than 36.6% in x = 0.6 alloy. It leads to an improvement of soft magnetic property by decreasing the H<sub>c</sub>, the P<sub>u</sub>, and increasing the μ<sub>i</sub> and the μ<sub>m</sub> of x = 0.8 alloy. Energy dispersive spectroscopy (EDS) result shows that, in both FeCoNiAl<sub>0.6</sub> (x = 0.6) and FeCoNiAl<sub>0.8</sub> (x = 0.8) alloys, the enrichment of Fe and Co elements and the depletion of Ni and Al elements are observed in FCC phase, while Fe and Co elements are depleted and Ni and Al elements are enriched in BCC phase. Moreover, a close value of ferromagnetic elements, (Fe + Co + Ni)%, is obtained in FCC phase (≈85%) and BCC phase (≈78%) in both FeCoNiAl<sub>0.6</sub> (x = 0.6) and FeCoNiAl<sub>0.8</sub> (x = 0.8) alloys. Combined with results of EDS and magnetic properties of x = 0.6 and x = 0.8 alloys, it can conclude that the saturation magnetization (M<sub>s</sub>) of BCC phase is larger than that of FCC phase.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering