Abstract:This work demonstrated the combination of the self-assembly of a block copolymer with the well-established non-solvent induced phase separation process. Nanoporous films were obtained with well-ordered cylinder pores perpendicular to the film surfaces on top of a non-ordered bicontinous porous layer. Numerous parameters during the film formation process, including the concentration of casting solution, the solvent evaporation time, the temperature of precipitation bath, and the gate height of doctor blade, were systematically investigated to realize the effective control of surface morphology. Voronoi tessellation was first introduced to quantitatively describe the regularity of the surface pattern. It was found that the concentration of casting solution and the solvent evaporation time have synergetic influences on the porous structures. With the increase of concentration, the minimum evaporation time needed for a well-ordered porous surface decreases. If keep the concentration as a constant, the evolution of surface morphologies from non-ordered cylinder pores to ordered cylinder pores, and then to lamellar pores, was observed with the increase of evaporation time. Although lots of combinations of these two parameters can be utilized for the well-ordered structure formation, the mean pore size of the film surface didn't change significantly with the change of film preparation conditions. Besides, the decrease of the temperature of precipitation bath also helped to improve surface pattern regularity. Further study revealed that once the gate height of casting solution was decreased, the evaporation of solvent induced more significant change of casting solution concentration and the solvent composition, resulting in the disappearance of well-ordered cylinder pores. Two ways, including decreasing the solvent evaporation time and applying the solvent annealing process, were proven to be very effective to prepare thinner films with well-ordered nanoporous structures. The above results greatly broaden the operation window and provide possibilities to fabricate films suitable for different applications.

Formation of Continuous Cubic Mesoporous Films by Spin Casting

Structural Control of Surfactant-Templated Hexagonal, Cubic, and Lamellar Mesoporous Silicate Thin Films Prepared by Spin-Casting

Continuous Mesoporous Silica Films with Highly Ordered Large Pore Structures

Effects of Coating Methods on Microstructure and Optical Properties of Mesoporous Silica Films

Controlling Pore Size and Wettability of A Unique Microheterogeneous Copolymer Film with Porous Structure

Synthesis of Continuous Mesoporous Silica Thin Films with Three-Dimensional Accessible Pore Structures

Stabilizing Surfactant Templated Cylindrical Mesopores In Polymer And Carbon Films Through Composite Formation With Silica Reinforcement

Growth of mesoporous materials within colloidal crystal films by spin-coating

The Effect of Water Content on the Preparation of Mesoporous Monoliths and Films

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Thermal Stability of Structurally Controlled Lamellae and Hexagonal Mesoporous Silicate Thin Films

Silica‐Templated Continuous Mesoporous Carbon Films by a Spin‐Coating Technique

Continuous Formation of Supported Unusual Mesostructured Silica Films by Sol−Gel Dip Coating

Oriented Zeolite Mfi Monolayer Films on Metal Substrates by in Situ Crystallization

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Achievement of thick mesoporous TiO2 crystalline films by one-step dip-coating approach

Synthesis of crack-free silica monoliths with cubic mesostructures by a fast evaporation process

A Reliable Synthesis of Cubic Mesoporous MCM-48 Molecular Sieve

Synthesis and Phase Behaviors of Bicontinuous Cubic Mesoporous Silica from Triblock Copolymer Mixed Anionic Surfactant

Synthesis of siliceous hollow spheres with large mesopore wall structure by supercritical CO2-in-water interface templating.

Preparation and Morphology Control of Highly Ordered Nanoporous Films from Block Copolymers