Abstract:Mesoporous silica with Ia (3) over bard structure has been successfully prepared by using mixed surfactants of commercially available nonionic block copolymer P123 (EO(20)PO(70)EO(20)) and anionic sodium dodecyl sulfate (SDS) as structure-directing agents through an acid-catalyzed silica sol-gel process. XRD, TEM, and N(2) sorption measurements show that the products have highly ordered bicontinuous cubic mesostructure with high surface area (similar to 770 m(2)/g), large pore volume (similar to 1.5 cm(3)/g) and uniform pore size (similar to 10 nm). Effects of preparation parameters on the formation of the mesostructure have been extensively investigated. It is found that the molar ratios of SDS/P123 between 2.1 and 2.5 and that of silicic species to P123 in the range from 40 to 75 are favorable for the formation of highly ordered Ia (3) over bard mesostructure. Prolonging hydrothermal treatment time leads to almost unchanged cell parameters of the products, whereas there is obvious increase of the pore sizes and pore volume. The results show that resultant template-free mesoporous silica products have excellent thermal stability, and they are more stable in N2 atmosphere than in air. Morphologies of the resultant materials can be further controlled by adding inorganic salt (such as Na(2)SO(4)) into the mixed surfactants system. Coral- and petaline-like mesoporous silica with continuous skeletons can be obtained. Understanding this synthesis system might be useful for economical and large-scale production of mesoporous materials with controllable structures.

Synthesis of Continuous Mesoporous Silica Thin Films with Three-Dimensional Accessible Pore Structures

Continuous Mesoporous Silica Films with Highly Ordered Large Pore Structures

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Mesoporous Structure Control of Silica in Room-Temperature Synthesis under Basic Conditions

Synthesis of siliceous hollow spheres with large mesopore wall structure by supercritical CO2-in-water interface templating.

Synthesis of silica mesoporous crystals with controlled structure and morphology using gemini surfactant

Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

Preparation of Ordered 2-D Hexagonal Mesoporous Silica with Ultra Thick Pore Walls Using a Novel Nonionic Organosilicon Surfactant

Formation of Continuous Cubic Mesoporous Films by Spin Casting

Synthesis of Mesoporous Silica with A Three-Dimensional Hexagonal Ordered Structure Using Cationic and Amphoteric Mixed Surfactants

Synthesis of carboxylic group functionalized mesoporous silicas (CFMSs) with various structures

Fabrication of Dimensional and Structural Controlled Open Pore, Mesoporous Silica Topographies on a Substrate

Large-Pore Mesoporous Silica with Three-Dimensional Wormhole Framework Structures

Emulsion droplets as a dynamic interface for the direct and large-scale synthesis of ultrathin free-standing mesoporous silica films as well as 2D polymeric and carbon nanomaterials.

Synthesis of Microporous Silica in the Presence of Dodecyldimethylbenzylammonium Chloride Surfactant

Structural Control of Surfactant-Templated Hexagonal, Cubic, and Lamellar Mesoporous Silicate Thin Films Prepared by Spin-Casting

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

A tri-continuous mesoporous material with a silica pore wall following a hexagonal minimal surface

Syntheses of High-Quality Mesoporous Materials Directed by Blends of Nonionic Amphiphiles under Nonaqueous Conditions

Growth of Mesoporous Silica Film with Vertical Channels on Substrate Using Gemini Surfactants