Abstract:A surfactant-templated silica xerogel with high pore volume, high porosity and narrow bimodal mesopore size distribution (designated as BMS) was synthesized by a judiciously controlled two-phase sol–gel processing under basic conditions. The properties of BMS silica mesostructure and the effect of ammonia/silica molar ratio on the resultant silica structure and morphology were assessed using various analytical techniques such as XRD, 29Si MAS NMR, SEM, TEM, TG-DTA and N2 adsorption measurements. It is found that BMS silica xerogel consists of the packing of the micelle-encapsulated nanometer silica particles in the 20–40 nm range, depending upon the ammonia/silica molar ratio, and shows both an intraparticle framework mesopore resulting from the surfactant removal and a textural mesopore resulting from the interparticle voids, which can be adjusted in the 12.6–34.8 nm range by varying just the ammonia/silica molar ratio. The textural pore volumes for all BMS silica can be two or more times as large as the framework pore volumes, and the fill of a certain amount of surfactant between interparticle voids in as-synthesized BMS silica xerogel may play a crucial role for the formation, stability and ordering of textural mesoporosity. A fast hydrolysis and slow condensation process is beneficial to the formation of BMS silica mesostructure. Following a gradual increase of ammonia/silica molar ratio, thus an increase of condensation rate, the mesostructure evolution of the resultant silica products obtained from a bimodal mesopore via a disordered mesopore to a well-defined ordered hexagonal mesopore MCM-41 was observed.

The Effect of Water Content on the Preparation of Mesoporous Monoliths and Films

Synthesis of crack-free silica monoliths with cubic mesostructures by a fast evaporation process

Effects of Coating Methods on Microstructure and Optical Properties of Mesoporous Silica Films

Thermal Stability of Structurally Controlled Lamellae and Hexagonal Mesoporous Silicate Thin Films

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes

Controlling Pore Size and Wettability of A Unique Microheterogeneous Copolymer Film with Porous Structure

A Fast Way for Preparing Crack-Free Mesostructured Silica Monolith

Oriented Zeolite Mfi Monolayer Films on Metal Substrates by in Situ Crystallization

Understanding of the High Hydrothermal Stability of the Mesoporous Materials Prepared by the Assembly of Triblock Copolymer with Preformed Zeolite Precursors in Acidic Media

Formation of Continuous Cubic Mesoporous Films by Spin Casting

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

Preparation and humidity control performance of aluminum containing mesoporous molecular sieve synthesis from liquid crystal display waste glass and sandblasting waste

Temperature-Driven Structural Evolution during Preparation of MCM-41 Mesoporous Silica

Structural Control of Surfactant-Templated Hexagonal, Cubic, and Lamellar Mesoporous Silicate Thin Films Prepared by Spin-Casting

Effects of Ammonia/silica Molar Ratio on the Synthesis and Structure of Bimodal Mesopore Silica Xerogel

A Systematic Investigation Of The Formation Of Ordered Mesoporous Silicas Using Poly(Ethylene Oxide)-B-Poly(Methyl Methacrylate) As The Template

Facile Synthesis of Transparent Mesostructured Composites and Corresponding Crack-Free Mesoporous Carbon/Silica Monoliths

Stabilizing Surfactant Templated Cylindrical Mesopores In Polymer And Carbon Films Through Composite Formation With Silica Reinforcement

Effect of organic hydrophobic groups on the pore structure and thermal properties of waterglass-based silica xerogels

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Preparation and Characterization of Macroporous Mayenite Monoliths