Application Of New Colloidal Forming

Yong Huang,Jinlong Yang

DOI: https://doi.org/10.1007/978-981-15-1872-0_6

2011-01-01

Abstract:The colloidal forming process based on gel-casting was applied for preparing microbeads of ceramics, improving the breakdown strength of rutile capacitor, developing the thin-wall rutile tube for ozone generator, and producing the refractory nozzle of zirconia (ZrO2) and lead zirconate titanate (PZT). The microbeads of ceramics were used as grinding media, gel-pen-ball and healthcare product with far infrared function for human body. Owing to the low-cost associated with the production of the gel-beads as well as because of its superior properties, they have been widely used and marketed.When compared with the extrusion forming, the breakdown strength of rutile capacitor prepared by gel-casting was improved greatly. The rutile ceramics with high dielectric constant and high breakdown strength have been used in thin-wall tube of ozone generator.ZrO2 refractory nozzle prepared by gel-casting has a high melting point above 2680 degrees C and a good thermal shock resistance to withstand the temperature rising from the room temperature to 2200 degrees C in several seconds. Hence, it is considered as a suitable material for making the nozzle for precision casting of Cu-Cr molten alloy.When compared with die pressing, gel-casting can provide a more homogenous microstructure as well as better piezoelectric property of the PZT samples. By using the same sintering procedure, gelcast samples were observed to exhibit slightly stronger piezoelectric effects than the die pressed ones. This may be attributed to both density difference and pore size.