Abstract:Gelcasting is a new ceramic forming technology for making complex-shaped ceramic products with high performance. The processes used in gelcasting are similar to processes often used in conventional ceramic forming process. However, when new high performance materials are introduced with the aim to improve the strength, defects such as air bubbles or agglomerates that can be found in many traditional ceramic materials are no longer be allowed since this would reduce the performance and reliability of the final ceramic products. The aim of this thesis project was to find an appropriate recipe of the ceramic suspension meanwhile improving the process of gelcasting and obtaining ceramic products with excellent mechanical behavior. To achieve this specified target, alumina and zirconia powders were studied in the following experiments which included rheological measurement of viscosity and storage modulus measurement for ceramic suspensions and drying shrinkage measurement of cast materials. The binder was burned out and the density was measured for ceramic materials sintered at different temperatures. The mechanical strength of sintered materials with high density was evaluated and the microstructure of fracture surfaces of ceramic samples was studied. Through rheological measurement, a good balance between fluidity and solid content of ceramic suspension was found. For alumina suspensions a solid content of 55vol% was selected and for zirconia solid contents of 46, 48 and 50vol% were studied. A monomer was dissolved in the suspension and an initiator was added to facilitate the polymerization of the monomer when the temperature was increased to around 70oC. The failure analysis of the fractured bending bars showed that the defects that caused the failure were not air bubbles but agglomerates. As a result, in future research for ceramic gelcasting with the intention to improve the mechanical strength, the suggestion is to use an appropriate recipe for the ceramic suspension and focus on elimination of granules and agglomerates from the suspension

Gelcasting of a Rutile Mixture Applied to Extrusion Forming

Preparing concentrated suspension of rutile mixture containing many additives

Gel Casting of High Strength Ceramics

Gelcasting of ceramic suspension in acrylamide/polyethylene glycol systems

Gelcasting of Aqueous Mesocarbon Microbead Suspension

Study On Gel-Tape Casting In The Mixed Polyvinyl Alcohol And Acrylamide Systems

Improved Gelcasting

Suppression of Surface-Exfoliation by Gelcasting Ceramics with Mixed Polymer-Monomer Solutions

Application Of New Colloidal Forming

Preparation of High Concentrated Suspension and Gelcasting Process for Silicon Nitride Bonded Silicon Carbide Refractories

Gelcasting of alumina ceramics in the mixed acrylamide and polyacrylamide systems

GELCASTING OF ALUMINA SLURRY DISPERSED IN SILICA SOL WITHOUT DE-AIRING PROCESS

Fabrication of complicated ceramic parts by gelcasting based on additive manufactured acetone-soluble plastic mold

Study on the Process of Si3N4 Ceramic with High Properties by Gel-casting

Ceramic in-situ forming based on gelation of sodium alginate

Study on Gelcasting of Silicon Nitride-Bonded Silicon Carbide Refractories

Gel-casting Without De-Airing Process Using Silica Sol As a Binder

Preparation of Ultrafine Zirconia Suspension for Gelcasting

Room-temperature Gelcasting of Alumina with Tartaric Acid and Glutaraldehyde

Gelcasting of Alumina with a Mixed PVP–MAM System

Fabrication, sintering behavior and mechanical properties of calcium oxide doped yttrium oxide refractory via aqueous gel casting method