Abstract:Based on the continuum damage mechanics model (CDM) for monotonic tension, a new CDM for ultra-low-cycle fatigue (ULCF) is put forward to predict ULCF damage of steel and its weld joint under strong earthquakes. The base metal, heat-affected zone and weld metal of Q345qC steel were considered as research objects, and the uniaxial plastic strain threshold of the CDM model was calibrated via tensile testing combined with finite element analysis of notched round bar specimens. ULCF tests of the base metal and weld specimens were carried out to analyse their fatigue life, fracture life and post-fracture path. Based on the calibrated uniaxial plastic strain threshold, the finite element models of base metal and weld specimens suitable for CDM model were established by ABAQUS. The calibration results of material parameters show that the weld metal has the lowest plastic strain threshold and the largest dispersion coefficient at the plastic strain threshold. Prediction results under cyclic loading with a large strain were compared with experimental values, and results showed that the predicted crack initiation and fracture lives of the base metal and weld specimens are lower than their corresponding experimental values. The predicted errors of crack initiation life and fracture life decrease with increasing strain level. The development law of the damage variable reveals exponential growth combined with a stepped pattern. The CDM model can also accurately predict the number of cycles to initial damage. Taking the results together, the CDM of the ULCF of the base metal and weld specimens could successfully predict post-fracture paths.

A damage mechanics-based fatigue life prediction approach for 30crmnsia alloy steel with impact defect

Study on the Prediction Method of the Ultra-Low-Cycle Fatigue Damage of Steel

Prediction of the Ultra-Low-Cycle Fatigue Damage of Q345qC Steel and Its Weld Joint

A Model for Ultra Low Cycle Fatigue Damage Prediction of Structural Steel

A Proposal on Ultra-Low Cycle Fatigue Damage Evaluation of Structural Steels

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Continuum Damage Mechanics Based Fatigue Life Prediction and Fatigue Property Analysis of Pitting Corrosion Steel Bars

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Assessment of prior fatigue damage and a new approach to predict remanent creep rupture of P92 steel

A crystal plasticity-based approach for creep-fatigue life prediction and damage evaluation in a nickel-based superalloy

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

Multiaxial Fatigue Life Prediction Based on Nonlinear Continuum Damage Mechanics and Critical Plane Method

New strain energy-based critical plane approach for multiaxial fatigue life prediction

A nonlinear cumulative fatigue damage life prediction model under combined cycle fatigue loading considering load interaction

Fatigue life prediction of aluminum alloy 6061 based on defects analysis

A new combined impact fatigue damage model and its application of influencing factors analysis on impact fatigue of TC18 titanium alloy

Numerical assessment on fatigue damage evolution of materials at crack tip of CT specimen based on CPFEM

A novel damage mechanics and XGBoost based approach for HCF life prediction of cast magnesium alloy considering internal defect characteristics

Fatigue life estimation of metal materials based on finite element analysis

Thermal-mechanical fatigue life prediction considering fatigue-creep interaction effects

Dislocation-based crystal plasticity modelling of a nickel-based superalloy under dwell-fatigue: From life prediction to residual life assessment