Study on the improvement of PVDF flat ultrafiltration membrane with MWCNTs-OH as the additive and the influence of different MWCNTs-OH scales
Wei Wang,Xin Xu,Zhichao Zhang,Peng Zhang,Yaping Shi,Ping Ding
DOI: https://doi.org/10.1016/j.colcom.2021.100433
IF: 5.633
2021-01-01
Colloid and Interface Science Communications
Abstract:Poly(vinylidene fluoride) (PVDF) ultrafiltration membrane has many advantages that make it widely applicated in water treatment. Still, the PVDF membrane's nature easy to pollute the defects, which makes it a severe threat to the further development of the PVDF membrane, which makes hydrophilic modification necessitated. Here we fabricated the PVDF-based blended matrix nanocomposite membranes using hydroxylated multi-walled carbon nanotubes (MWCNTs-OH) as the additive via low-temperature thermally induced phase separation (L-TIPS) method. Consequently, the addition of MWCNTS-OH significantly improved the pure water flux (from 365.38 L/(m2·h) to 617.24 L/(m2·h)), hydrophilicity, and anti-fouling property of the membrane, and gave PVDF membrane more potent mechanical properties. Besides, the influence of different tube diameters (<8 nm, 10-20 nm, 20-30 nm, 30-50 nm, >50 nm) of MWCNTS-OH on membrane properties were investigated and obtained the most suitable adding tube diameters of MWCNTS-OH: when the tube diameter of MWCNTs-OH was 10-20 nm; membrane surface roughness decreased from 0.354 μm to 0.071 μm, and the dynamic contact angle was the lowest among the membranes about 77.6°; flux recovery ratio (FRR) values were higher than 92% by adding MWCNTs-OH. Our research for the further development and optimization of PVDF membrane provides a new perspective.