Abstract:A Ni/scandia-stabilized zirconia (ScSZ) cermet anode was modified by coating with nano-sized gadolinium-doped ceria (GDC, Gd0.2Ce0.8O2) prepared using a simple combustion process within the pores of the anode for a solid oxide fuel cell (SOFC) running on methane fuel. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were employed in the anode characterizations. Then, the short-term stability for the cells with the Ni/ScSZ and 2.0wt.%GDC-coated Ni/ScSZ anodes in 97%CH4/3%H2O at 700°C was checked over a relative long period of operation. Open circuit voltages (OCVs) increased from 1.098 to 1.179V, and power densities increased from 224 to 848mWcm−2, as the operating temperature of an SOFC with 2.0wt.%GDC-coated Ni/ScSZ anode was increased from 700 to 850°C in humidified methane. The coating of nano-sized Gd0.2Ce0.8O2 particle within the pores of the porous Ni/ScSZ anode significantly improved the performance of anode supported cells. Electrochemical impedance spectra (EIS) illustrated that the cell with Ni/ScSZ anode exhibited far greater impedances than the cell with 2.0wt.%GDC-coated Ni/ScSZ anode. Introduction of nano-sized GDC particles into the pores of porous Ni/ScSZ anode will result in a substantial increase in the ionic conductivity of the anode and increase the triple phase boundary region expanding the number of sites available for electrochemical activity. No significant degradation in performance has been observed after 84h of cell testing when 2.0wt.%GDC-coated Ni/ScSZ anode was exposed to 97%CH4/3%H2O at 700°C. Very little carbon was detected on the anodes, suggesting that carbon deposition was limited during cell operation. Consequently, the GDC coating on the pores of anode made it possible to have good stability for long-term operation due to low carbon deposition.

Direct Feeding of Liquid Fuel in Sofc

Feasibility of n-Dodecane Fuel for Solid Oxide Fuel Cell with Ni-ScSZ Anode

Attempt of Utilizing Liquid Fuels with Ni?ScSZ Anode in SOFCs

Feasibility of Liquid Hydrocarbon Fuels for SOFC with Ni–ScSZ Anode

Stability of Ni Base Anode for Direct Hydrocarbon SOFCs

Feasibility of Ni-based cermet anode for direct HC SOFCs: Fueling ethane at a low S/C condition to Ni–ScSZ anode-supported cell

Effect of Ceria Components on Anode Performance of Ni-base Anode in Hydrocarbon Fueled SOFC

Solid-oxide Fuel Cell Operated on in Situ Catalytic Decomposition Products of Liquid Hydrazine

A high-performance Ni-CeO2/Ni/Ni-Y2O3·ZrO2 three-layer anode for direct iso-octane feeding of solid oxide fuel cells

Anode Degradation in SOFC: Fuel Impurity Effects on Nickel Component

Direct liquid methanol-fueled solid oxide fuel cell

Operation of ceria-electrolyte solid oxide fuel cells on iso-octane–air fuel mixtures

Direct-Methane Solid Oxide Fuel Cells with Hierarchically Porous Ni-Based Anode Deposited with Nanocatalyst Layer

Solid Oxide Fuel Cells Operated by Internal Partial Oxidation Reforming of Iso-Octane

Reaction Process in the Ni–ScSZ Anode for Hydrocarbon Fueled SOFCs

Performance of Ni/Scsz Cermet Anode Modified by Coating with Gd0.2ce0.8o2 for an Sofc Running on Methane Fuel

Controlled Deposition and Utilization of Carbon on Ni-Ysz Anodes of Sofcs Operating on Dry Methane

Anode Catalyst Layers for Direct Hydrocarbon and Internal Reforming SOFCs

Samaria-doped Ceria Modified Ni/YSZ Anode for Direct Methane Fuel in Tubular Solid Oxide Fuel Cells by Impregnation Method

Direct Electrolysis of CO2 in Solid Oxide Cells Supported on Ceramic Fuel Electrodes with Straight Open Pores and Coated Catalysts

Direct-methane Solid Oxide Fuel Cells with an in Situ Formed Ni–Fe Alloy Composite Catalyst Layer over Ni–YSZ Anodes