Abstract:A Ni/scandia-stabilized zirconia (ScSZ) cermet anode was modified by coating with nano-sized gadolinium-doped ceria (GDC, Gd0.2Ce0.8O2) prepared using a simple combustion process within the pores of the anode for a solid oxide fuel cell (SOFC) running on methane fuel. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were employed in the anode characterizations. Then, the short-term stability for the cells with the Ni/ScSZ and 2.0wt.%GDC-coated Ni/ScSZ anodes in 97%CH4/3%H2O at 700°C was checked over a relative long period of operation. Open circuit voltages (OCVs) increased from 1.098 to 1.179V, and power densities increased from 224 to 848mWcm−2, as the operating temperature of an SOFC with 2.0wt.%GDC-coated Ni/ScSZ anode was increased from 700 to 850°C in humidified methane. The coating of nano-sized Gd0.2Ce0.8O2 particle within the pores of the porous Ni/ScSZ anode significantly improved the performance of anode supported cells. Electrochemical impedance spectra (EIS) illustrated that the cell with Ni/ScSZ anode exhibited far greater impedances than the cell with 2.0wt.%GDC-coated Ni/ScSZ anode. Introduction of nano-sized GDC particles into the pores of porous Ni/ScSZ anode will result in a substantial increase in the ionic conductivity of the anode and increase the triple phase boundary region expanding the number of sites available for electrochemical activity. No significant degradation in performance has been observed after 84h of cell testing when 2.0wt.%GDC-coated Ni/ScSZ anode was exposed to 97%CH4/3%H2O at 700°C. Very little carbon was detected on the anodes, suggesting that carbon deposition was limited during cell operation. Consequently, the GDC coating on the pores of anode made it possible to have good stability for long-term operation due to low carbon deposition.

Feasibility of Ni-based cermet anode for direct HC SOFCs: Fueling ethane at a low S/C condition to Ni–ScSZ anode-supported cell

La0.6Sr0.4Co0.2Fe0.8O3-δ Nanoparticles Modified Ni-based Anode for Direct Methane-Fueled SOFCs

Performance of Ni/Scsz Cermet Anode Modified by Coating with Gd0.2ce0.8o2 for an Sofc Running on Methane Fuel

Direct-methane solid oxide fuel cells with an <i>in situ</i> formed Ni-Fe alloy composite catalyst layer over Ni-YSZ anodes

Direct-Methane Solid Oxide Fuel Cells with Hierarchically Porous Ni-Based Anode Deposited with Nanocatalyst Layer

Stability of Ni-YSZ Anode for SOFCs in Methane Fuel: the Effects of Infiltrating La0.8Sr0.2FeO3-δand Gd-Doped CeO2Materials

Methane-fueled SOFC with Traditional Nickel-Based Anode by Applying Ni/Al2O3 As a Dual-Functional Layer

NiCu–Zr0.1Ce0.9O2−δ Anode Materials for Intermediate Temperature Solid Oxide Fuel Cells Using Hydrocarbon Fuels

Robust Ni-based Anode Deposited with La0.6Sr0.4FeO3-δfor Direct Methane-Fueled SOFCs

Anode supported SOFC fabricated with functional anode: role of variation of fuel and oxidants

Enhanced coking resistance of a Ni cermet anode by a chromates protective layer

A high-performance Ni-CeO2/Ni/Ni-Y2O3·ZrO2 three-layer anode for direct iso-octane feeding of solid oxide fuel cells

A NiFeCu alloy anode catalyst for direct-methane solid oxide fuel cells

Controlled Deposition and Utilization of Carbon on Ni-Ysz Anodes of Sofcs Operating on Dry Methane

Solid-oxide Fuel Cell Operated on in Situ Catalytic Decomposition Products of Liquid Hydrazine

Coking-resistant Ce0.8Ni0.2O2-δ Internal Reforming Layer for Direct Methane Solid Oxide Fuel Cells

Low Nickel, Ceria Zirconia-Based Micro-Tubular Solid Oxide Fuel Cell: A Study of Composition and Oxidation Using Hydrogen and Methane Fuel

Anode Catalysts for Solid Oxide Fuel Cells That Run Directly on Hydrocarbon Fuels

Single-chamber solid oxide fuel cells with nanocatalyst-modified anodes capable of in situ activation

Fabrication and Performance of Direct Methane SOFC with a Cu-CeO2-Based Anode

Solid Oxide Fuel Cell Anode Materials for Direct Hydrocarbon Utilization