Abstract:A simple spray approach to fabricate superhydrophobic coatings on tile and glass substrates is presented. Commercial available polyphenylene sulfide (PPS) and hydrophobic silica (H-SiO(2)) powder were suspended in ethanol and the mixed suspensions were spray on substrates. After dried at different temperatures, surface coatings with different hydrophobicity were obtained. By observing the surface morphologies with scanning electron microscope (SEM) and atomic force microscope (AFM), and measuring water contact angles with a contact angle system, factors affecting the morphology, roughness and contact angle of the surface coatings, such as thermal treatment temperature and the weight ratio of H-SiO(2) to PPS, were investigated in detail. With the increase of the thermal treatment temperature, both the surface roughness and the contact angle increased when the temperature was lower than 280 degrees C. As the weight ratio of H-SiO(2) to PPS rose from 1: 10 to 1:1, more H-SiO(2) powders accumulated on the surface, leading to a significant increase of hydrophobicity. The surface coating obtained at 280 degrees C with the weight ratio of H-SiO(2) to PPS 1:1 showed a water contact angle higher than 150 degrees and a sliding angle lower than 4, exhibiting fascinating superhydrophobic properties. The surface coating could remain superhydrophobicity upon a further increase in thermal treatment temperature or the amount of H-SiO(2) powder. Moreover, the surface coatings showed high contact angles, larger than 150, for all the solutions with pH ranging from 1 to 14. The abrasion resistant property of the as-prepared superhydrophobic surface coating was tested using a homemade setup. Being scraped by freely-falling sands, the superhydrophobic coating could keep its high hydrophobicity, while a commercial hydrophobic coating transformed from hydrophobicity to hydrophilicity. This result implied our superhydrophobic surface coating was very stable. Moreover, chalk powders on the superhydrophobic surface coatings could easily be washed off with water, indicating good self-cleaning properties. The presented approach is convenient and can be potentially applied in fabrication of superhydrophobic surfaces in large scale.

Conductive and Transparent Superhydrophobic Films on Various Substrates by in Situ Deposition

Low-cost preparation of durable, transparent, superhydrophobic coatings with excellent environmental stability and self-cleaning function

Highly Transparent and Highly Hydrophobic Coating for Outdoor Camera Window Glass: Fabrication, Transparency, and Hydrophobicity

Fabrication and Super-Hydrophilic Property of Transparent Tio2/Sio2 Film from Sol-Gel Process

Transparent Superhydrophobic and Self-Cleaning Coating

Preparation of Transparent Antistatic Multifunctional Superhydrophobic Film

PREPARATION AND PROPERTIES OF SUPERHYDROPHOBIC POLYPHENYLENE SULFIDE COMPOSITE COATINGS

Mechanically Robust, Thermally Stable, Broadband Antireflective, and Superhydrophobic Thin Films on Glass Substrates

Facile Fabrication of Superhydrophobic Nanocomposite Coatings Based on Water‐Based Emulsion Latex

Facile Fabrication of Fluorine-Free, Transparent and Self-Cleaning Superhydrophobic Coatings Based on Biopolymer Castor Oil

Transparent and Durable SiO2‐containing Superhydrophobic Coatings on Glass

An Environmentally Friendly Approach for the Fabrication of Conductive Superhydrophobic Coatings with Sandwich-Like Structures

Rapid Fabrication of a Transparent Superhydrophobic Coating: Potential Application with Pollution-Free under Construction

Ultra-high performance flexible and controllable superhydrophobic films based on microsphere/micro-pyramid hierarchical arrays

One‐step Fabrication of Fluoropolymer Transparent Films with Superhydrophobicity by Dry Method

Fabrication of ultra-smooth hybrid thin coatings towards robust, highly transparent, liquid-repellent and antismudge coatings

Free-standing, flexible, multifunctional, and environmentally stable superhydrophobic composite film made of self-assembled organic micro/super-nanostructures through solution process.

Fabrication of superhydrophobic transparent coatings prepared by spraying dual-sized silica particles

Fabrication of Superhydrophobic Coatings by Using Spraying and Analysis of Their Anti-Icing Properties

Fabrication of Robust, Anti-reflective, Transparent Superhydrophobic Coatings with a Micropatterned Multilayer Structure

A multifunctional and environmentally-friendly method to fabricate superhydrophilic and self-healing coatings for sustainable antifogging