Xiaoqin Wang,Shuhui Li,Jianying Huang,Jiajun Mao,Yan Cheng,Lin Teng,Zhong Chen,Yuekun Lai

DOI: https://doi.org/10.1016/j.cej.2020.128228

IF: 15.1

2021-04-01

Chemical Engineering Journal

Abstract:<p>Antifogging films are essential in many areas, such as eyeglasses, windshields, goggles and so on. In this work, a transparent antifogging film was successfully prepared on glass by spin-coating a mixture of poly(acrylic acid) (PAA), carboxymethyl cellulose (CMC) and iron (III) chloride hexahydrate (FeCl₃·6H₂O). The coated film was superhydrophilic and showed excellent anti-frosting and self-healing properties. The composite coating was resistant to fouling by oil and had a very small water sliding angle about 3.1°. This coating could maintain its antifogging performance after by tape-peeling test for 80 cycles and being exposed to UV irradiation for 96 h. The diverse desirable functions demonstrated and the facile preparation procedure of the film offer huge potential in many practical applications.</p>

engineering, chemical, environmental

What problem does this paper attempt to address?

The paper aims to deal with the problem of fog formation on transparent surfaces. This can cause significant light scattering and a decrease in light transmission, bringing inconvenience and potential safety problems in various applications such as eyeglasses, windshields and goggles. In particular, the research focuses on developing a multifunctional and environmentally - friendly method to produce superhydrophilic and self - healing coatings with excellent antifogging and frost - resistant properties.

The main objectives of the paper are as follows:
- **Developing an Environmentally - Friendly Coating**: The coating is made of environmentally - friendly materials, namely carboxymethyl cellulose (CMC), poly(acrylic acid) (PAA) and iron(III) chloride hexahydrate (FeCl₃·6H₂O), in order to reduce potential environmental impacts.
- **Achieving Superhydrophilicity**: The coating is designed to be superhydrophilic, with a water contact angle (CA) of less than 5°. This enables condensed water droplets to spread into a uniform film, preventing fog formation.
- **Enhancing Durability and Robustness**: The coating is tested for its durability under various conditions, including UV irradiation, tape peeling and exposure to high temperatures, to ensure its practical applicability.
- **Incorporating Self - Healing Properties**: The coating is designed to self - heal from scratches when exposed to water vapor, maintaining its transparency and antifogging performance.
- **Improving Anti - Fouling Performance**