PREPARATION AND PROPERTIES OF SUPERHYDROPHOBIC POLYPHENYLENE SULFIDE COMPOSITE COATINGS

Wang Suhao,Li Mei,Su Bin,Lu Qinghua

DOI: https://doi.org/10.3724/sp.j.1105.2010.09124

2010-01-01

Acta Polymerica Sinica

Abstract:A simple spray approach to fabricate superhydrophobic coatings on tile and glass substrates is presented. Commercial available polyphenylene sulfide (PPS) and hydrophobic silica (H-SiO(2)) powder were suspended in ethanol and the mixed suspensions were spray on substrates. After dried at different temperatures, surface coatings with different hydrophobicity were obtained. By observing the surface morphologies with scanning electron microscope (SEM) and atomic force microscope (AFM), and measuring water contact angles with a contact angle system, factors affecting the morphology, roughness and contact angle of the surface coatings, such as thermal treatment temperature and the weight ratio of H-SiO(2) to PPS, were investigated in detail. With the increase of the thermal treatment temperature, both the surface roughness and the contact angle increased when the temperature was lower than 280 degrees C. As the weight ratio of H-SiO(2) to PPS rose from 1: 10 to 1:1, more H-SiO(2) powders accumulated on the surface, leading to a significant increase of hydrophobicity. The surface coating obtained at 280 degrees C with the weight ratio of H-SiO(2) to PPS 1:1 showed a water contact angle higher than 150 degrees and a sliding angle lower than 4, exhibiting fascinating superhydrophobic properties. The surface coating could remain superhydrophobicity upon a further increase in thermal treatment temperature or the amount of H-SiO(2) powder. Moreover, the surface coatings showed high contact angles, larger than 150, for all the solutions with pH ranging from 1 to 14. The abrasion resistant property of the as-prepared superhydrophobic surface coating was tested using a homemade setup. Being scraped by freely-falling sands, the superhydrophobic coating could keep its high hydrophobicity, while a commercial hydrophobic coating transformed from hydrophobicity to hydrophilicity. This result implied our superhydrophobic surface coating was very stable. Moreover, chalk powders on the superhydrophobic surface coatings could easily be washed off with water, indicating good self-cleaning properties. The presented approach is convenient and can be potentially applied in fabrication of superhydrophobic surfaces in large scale.