Abstract:In this paper, the Sialon phase was synthesized under the conditions of ultra-high pressure (5.5 GPa) and high temperature (1550 degrees C), and the polycrystalline cubic boron nitride (PcBN) composite was in situ synthesized with TiB2, AlN, Sialon as the binder of cubic boron nitride (cBN). X-ray diffractometry (XRD), universal testing machine, field emission scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and transmission electron microscopy (TEM) were used to study the effects of Sialon rod crystal on the phase composition, microstructure and mechanical properties of PcBN composites. The results show that when TiB2 rod crystal is formed in the system, the irregular long rod-like new phase Sialon grows along the [0001] face appears. The mechanics properties and machinery properties of the sintered body were significantly improved due to the formation of Sialon. When the generation amount of Sialon is 30 %, the aspect ratio of Sialon is 3/1- 4/1 at most, with high hardness and strength of 27.49 GPa and 903.741 MPa, respectively, as well as the fracture toughness and wear are relatively favorable, separately 7.387 MPa.m(1/2) and 1602, the interface is well bonded and the density is the highest. At this time, the comprehensive performance of the PcBN composite material is most superior.

Submicron Cubic Boron Nitride As Hard As Diamond

Superhard solid solutions of diamond and cubic boron nitride

Preparation of superhard cubic boron nitride sintered from commercially available submicron powders

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Sintering of Fine Grained Polycrystalline Cubic Boron Nitride Compacts Without Binder

High-pressure Synthesis of Tungsten Carbide–cubic Boron Nitride (wc–cbn) Composites: Effect of Cbn Particle Size and Volume Fraction on Their Microstructure and Properties

Superhard Composites of Cubic Silicon Nitride and Diamond

Ultrahard stitching of nanotwinned diamond and cubic boron nitride in C 2 -BN composite

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Micro-sized polycrystalline cubic boron nitride with properties comparable to nanocrystalline counterparts

Small onion-like BN leads to ultrafine-twinned cubic BN

Polycrystalline Cubic Boron Nitride Prepared with Cubic-Hexagonal Boron Nitride under High Pressure and High Temperature

Ultrahard Nanotwinned Cubic Boron Nitride.

Ultrahard and Stable Nanostructured Cubic Boron Nitride from Hexagonal Boron Nitride

Hardness and Thermal Stability Enhancement of Polycrystalline Diamond Compact Through Additive Hexagonal Boron Nitride

In situ high pressure synthesis of cBN-based composites

Hardness of Polycrystalline Wurtzite Boron Nitride (wBN) Compacts

Characterization of Polycrystalline Cbn Compacts Sintered Without Any Additives

Hard and tough ultrafine-grained B4C-cBN composites prepared by high-pressure sintering

Synthesis and Characterization of Novel Ti3SiC2–cBN Composites

In situ synthesis of PcBN composites by Sialon combined with cBN-TiB2-AlN and their properties