Abstract:Multiferroic ceramics were prepared and characterized in (1-x)BiFeO3-x(0.5CaTiO(3)-0.5SmFeO(3)) system by a standard solid-state reaction process. The structure evolution was investigated by X-ray diffraction and Raman spectrum analyses. The refinement results confirmed the different phase assemblages with varying amounts of polar rhombohedral R3c and nonpolar orthorhombic Pbnm as a function of the substitution content. In the compositions range of 0.2x0.5, polar R3c and nonpolar Pbnm coexisted, which was referred to polar-to-nonpolar morphotropic phase boundary (MPB). According to the dielectric and DSC analysis results, the ceramics with x0.2 changed to diffused ferroelectric, and the ferroelectric properties were enhanced significantly. Two dielectric relaxations were detected in the temperature range of 200-300 K and 500-700 K, respectively. The high-temperature dielectric relaxation was attributed to the grain-boundary effects. While the low temperature dielectric relaxation obtained in the samples with x=0.3-0.5 was related to the charge transfer between Fe2+ and Fe3+. The magnetic hysteresis loops measured at different temperature indicated the enhanced magnetic properties in the present ceramics, which could be attributed to the suppressed cycloidal spin magnetic structure by Ti ions. In addition, the rare-earth Sm spin moments might also affect the magnetic properties at relatively lower temperature.

Large Polarization and Enhanced Magnetic Properties in Bifeo3 Ceramic Prepared by High-Pressure Synthesis

Large electric‐field‐induced strain and enhanced piezoelectric constant in CuO‐modified BiFeO3‐BaTiO3 ceramics

Room Temperature Ferroelectric, Ferromagnetic and Magnetoelectric Properties of Ba-Doped Bifeo3 Thin Films

Larger Polarization and Weak Ferromagnetism in Quenched Bifeo3 Ceramics with A Distorted Rhombohedral Crystal Structure

Preparation and Multi-Properties of Insulated Single-Phase Bifeo3 Ceramics

Room-Temperature Saturated Ferroelectric Polarization In Bifeo3 Ceramics Synthesized By Rapid Liquid Phase Sintering

The evolution of structure, properties and polar domains in rare earth and PbTiO3 co-substituted BiFeO3 ferroelectric ceramics

Polar Order Evolutions Near the Rhombohedral to Pseudocubic and Tetragonal to Pseudocubic Phase Boundaries of the Bifeo3-Batio3 System

The development of BiFeO 3 -based ceramics

The development of BiFeO3-based ceramics

Enhanced Dielectric and Multiferroic Properties of Single-Phase Y and Zr Co-Doped Bifeo3 Ceramics

Structural Evolution, Electrical Properties and Electric-Field-induced Changes of (0.8− X )pbtio 3 – X BiFeO 3 –0.2bazro 3 System Near the Morphotropic Phase Boundary

Structure of BiFeO3 ceramics treated with hot-pressing

Ferroelectric and Magnetic Properties in (1-X)bifeo3-x(0.5catio(3)-0.5smfeo(3)) Ceramics

MnO2-doping Induced Enhanced Multiferroicity in Bi0.83Sm0.17Fe0.95Sc0.05O3 Ceramics

Processing And Ferroelectric Properties Of Ti-Doped Bifeo3 Ceramics

Structural and electrical properties of multiferroic (1−x)BiFeO3−xBi0.5K0.5TiO3 ceramics

Electrical and magnetic properties of single-phased and highly resistive ferroelectromagnet BiFeO<sub>3</sub> ceramic

Synthesis and properties of multiferroic BiFeO 3 ceramics

Synthesis and Properties of Multiferroic Bifeo3 Ceramics

Ferroelectric and Magnetic Properties in High-Pressure Synthesized BiFeO3 Compound