Large electric field-induced strain in BiFeO3-based ceramics by tuning defect dipoles and phase structure
Fangfang Zeng,Yangyang Zhang,Zhengkai Tu,Xu Ge,Fei Wang,Mengmeng Hao,Jianjia Zhang,Yanjiong Wang,Xin Chen,Wenzhong Lu,Guifen Fan
DOI: https://doi.org/10.1016/j.ceramint.2021.01.280
IF: 5.532
2021-05-01
Ceramics International
Abstract:<p>High-performance lead-free piezoelectric materials with high Curie temperature can be used as substitutes for lead-based piezoelectric components to address serious environmental issues. In our works, 0.7Bi<sub>1.05</sub>Fe<sup>+3</sup><sub>(1−<em>x</em>)</sub>Fe<sup>2+</sup><sub><em>x</em></sub>O<sub>3−δ</sub>– 0.3BaTiO<sub>3</sub> (BF–BT–<em>x</em>Fe<sup>2+</sup>) ceramics, which demonstrate outstanding large-signal piezoelectric coefficient of <em>d</em><sub>33</sub>* = 510 p.m./V and electric field-induced bipolar strain of Δs<sub>p−p</sub> = 0.34% (peak-to-peak) at 50 kV/cm. Meanwhile, optimal remanent polarization of <em>P</em><sub>r</sub> = 55.8 μC/cm<sup>2</sup>, piezoelectric coefficient of <em>d</em><sub>33</sub> = 178 pC/N, and Curie temperature of <em>T</em><sub><em>c</em></sub> = 485 °C are achieved at <em>x</em> = 0.07. Of particular interesting the preferred strain is observed in BF–BT–<em>x</em>Fe<sup>2+</sup> ceramics with major pseudo-cubic phase. Results showed that prior electric properties are derived from synergistic effect of defect dipoles and phase structure together with non-180° domain switch. The defect dipole builds an internal electric field that favors ferroelectric domain formation and polarization. In addition, the formation of defect breaks the geometry symmetry of cubic structure.</p>
materials science, ceramics