Abstract:In this study, integrated experimental tests and computational modeling are proposed to investigate the failure mechanisms of open-hole cross-ply carbon fiber reinforced polymer (CFRP) laminated composites. In particular, we propose two effective methods, which include width-tapered double cantilever beam (WTDCB) and fixed-ratio mixed-mode end load split (FRMMELS) tests, to obtain the experimental data more reliably. We then calibrate the traction-separation laws of cohesive zone model (CZM) used among laminas of the composites by leveraging these two methods. The experimental results of fracture energy, i.e. G Ic and G Tc , obtained from WTDCB and FRMMELS tests are generally insensitive to the crack length thus requiring no effort to accurately measure the crack tip. Moreover, FRMMELS sample contains a fixed mixed-mode ratio of G IIc /G Tc depending on the width taper ratio. Examining comparisons between experimental results of FRMMELS tests and failure surface of B-K failure criterion predicted from a curve fitting, good agreement between the predictions and experimental data has been found, indicating that FRMMELS tests are an effective method to determine mixed-mode fracture criterion. In addition, a coupled experimental-computational modeling of WTDCB, edge notched flexure, and FRMMELS tests are adopted to calibrate and validate the interfacial strengths. Finally, failure mechanisms of open-hole cross-ply CFRP laminates under flexural loading have been studied systematically using experimental and multi-scale computational analyses based on the developed CZM model. The initiation and propagation of delamination, the failure of laminated layers as well as load-displacement curves predicted from computational analyses are in good agreement with what we have observed experimentally.

A Study of Failure Strength for Fiber-Reinforced Composite Laminates with Consideration of Interface

Micro Failure Analysis of Fiber Metal Laminates

Initial and Final Failure Strength Analysis of Composites Based on a Micromechanical Method

Interaction of Multiple Micro-Defects on the Strength and Failure Mechanism of UD Composites by Computational Micromechanics

An elastic-plastic cohesive zone model for metal-ceramic interfaces at finite deformations

Shear Deformation Of A Composite Until Failure With A Debonded Interface

A High-Efficient Model for Interface Debonding Analysis of Carbon Fiber-Reinforced Polymer Composite

Micromechanical Progressive Damage Analysis of Inter- and Intra-Layer Failures in Fiber-Reinforced Composite Laminates

Numerical Investigations of Microscopic Characteristic Influences on the Mechanical Properties of Polymer‐matrix Composites

Prediction of Interfacial Debonding in Fiber‐Reinforced Composite Laminates

Failure Analysis of Composite Laminate under Low-Velocity Impact Based on Micromechanics of Failure

Working Temperature Variation Effect on the Failure Envelope of Continuous Fiber-Reinforced Composites

Micromechanical analysis of off-axis loading of fiber reinforced composites with imperfect interface bonding

On Strength Prediction of Laminated Composites

Failure Locus Analysis Of Fibre-Reinforced Composites Under Combined Transverse Stresses Through Computational Micromechanics

Micromechanical Modeling of Longitudinal Tensile Behavior and Failure Mechanism of Unidirectional Carbon Fiber/aluminum Composites Involving Fiber Strength Dispersion

An insight into the mechanical behavior and failure mechanisms of T-stiffened composite structures with through-interface debonding defects

An Integrated Constitutive Model for Tensile Failure Analysis and Overlap Design of Adhesive-Bonded Composite Joints

Failure Modes of a Laminated Composite With Complaint Interlayers

A Combined Experimental and Computational Analysis of Failure Mechanisms in Open-Hole Cross-ply Laminates under Flexural Loading

The Dependence of the Fracture Toughness of Thermoplastic Composite Laminates on Interfacial Interaction