Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

Failure Locus Analysis Of Fibre-Reinforced Composites Under Combined Transverse Stresses Through Computational Micromechanics

Micro Failure Analysis of Fiber Metal Laminates

Progressive failure analysis of 2D woven composites at the meso-micro scale

Interaction of Multiple Micro-Defects on the Strength and Failure Mechanism of UD Composites by Computational Micromechanics

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

Comprehensive inter-fibre failure analysis and failure criteria comparison for composite materials using micromechanical modelling under biaxial loading

Micromechanical modeling for longitudinal tensile property of unidirectional CFRP considering dispersion of fiber properties

A 3D Micromechanics-Based Failure Criterion for Fiber Reinforced Composites under Longitudinal Compression

Modification of the model for calculating the long SiC fibre-reinforced metal matrix composites transverse strength and study for interfacial influences

Failure analysis of unidirectional FRP with fiber clusters under transverse pure shear

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

Initial Damage Induced by Thermal Residual Stress and Microscopic Failure Analysis of Carbon-Fiber Reinforced Composite under Shear Loading

A Microscopic Elasto-Plastic Damage Model for Characterizing Transverse Responses of Unidirectional Fiber-Reinforced Polymer Composites

Effect of resin-rich areas on failure behavior of unidirectional CFRP under transverse pure shear

Micromechanical Modeling of Damage Evolution and Mechanical Behaviors of CF/Al Composites under Transverse and Longitudinal Tensile Loadings.

Failure analysis of unidirectional fiber reinforced plastics based on computational micromechanics and PUCK failure theory

A Combined Experimental and Computational Analysis of Failure Mechanisms in Open-Hole Cross-ply Laminates under Flexural Loading

Micromechanical analysis of stochastic fiber/matrix interface strength effect on transverse tensile property of fiber reinforced composites

Prediction of the inter-fiber mechanical properties of composites: Part II Failure criterion based on micromechanics and cross-scale stress calculation

Progressive Damage and Failure Modeling in Fiber-Reinforced Laminated Composites Containing a Hole

Microscopic Progressive Damage Simulation of Unidirectional Composite Based on the Elastic–plastic Theory