Abstract:The polymerization of styrene (St) with a modified rare earth catalyst system composed of neodymium tricarboxylate (Nd), triisobutyl aluminium (Al) and n-butyl chloride (BCL) was carried out in cyclohexane. The effects of preparation procedure of the catalyst system (the molar ratios of Al/Nd and of BCL/Nd, ageing temperature and ageing time) and reaction conditions (catalyst concentration, polymerization temperature and polymerization time) on St polymerization, catalytic activity, molecular weight and molecular weight distribution of the resultant polymers were investigated. The catalytic activity depended mainly on the molar ratios of Al/Nd and BCL/Nd, the catalyst concentration, the polymerization temperature and time. High molecular weight. of polystyrene could be obtained with the catalyst with low Al/Nd and BCL/Nd ratios aged at relatively low temperature for relatively short time. The molecular weight of polymers increased with a decrease in polymerization temperature. The optimum conditions for obtaining high molecular weight polystyrene are as follows: Al/Nd = 8 similar to 12 (molar ratio), BCL/Nd = 5 similar to 25 (molar ratio), T = 40 similar to 50 degrees C, t(a) = 6 similar to 20 h, Nd/St = 1.5 x 10(-4) similar to 6.0 x 10(-4) ( molar ratio), TP = 40 similar to 50 degrees C. The molecular weight of the polymers reached high weight-average (M) values (M-W = 7.6 x 10(5) g mol(-1)) when Al/Nd = 10. The molecular weight decreased and molecular weight distribution became broad when excess Al or BCL existed in the catalyst system. The polymer obtained was extracted by 2-butanone and then separated into an insoluble fraction and a soluble fraction. The DSC characterization of the insoluble fraction shows that its melting point is around 268 degrees C, which indicating that the insoluble fraction mainly contains syndiotactic polystyrene. It is shown from polarized optical micrograph that the soluble fraction also contains some segments with high stereoregularity.

Synthesis and Characterization of Random Styrene–butadiene Copolymer with Nd-based Catalyst

"One-Pot" Random Terpolymerization Of Styrene, Isoprene And Butadiene With Nd-Based Catalyst

Styrene polymerization with ternary neodymium-based catalyst system: effects of catalyst preparation procedures

Synthesis of structured nanoparticles of styrene/butadiene block copolymers via RAFT seeded emulsion polymerization

Copolymerization of Butadiene and Styrene with Neodymium Naphthenate Based Catalyst

Selective polymerization of butadiene in styrene catalyzed by neodymium phosphonate

Synthesis of High Cis-1,4 Polybutadiene with Narrow Molecular Weight Distribution by Nd-Based Catalyst in the Presence of Styrene

Copolymerization of Butadiene with Styrene by Nd(vers)3–Al(i‐Bu)3–CHCl3Catalyst System

The Effect of [pph3]/[ni] in the Synthesis of SBS Via Changing Catalytic Active Centers from A Novel Synthetic Strategy for Styrene–butadiene–styrene Tri-Block Copolymer with High Cis-1,4 Units Via Changing Catalytic Active Centres

The terpolymer of neodymium‐catalyzed styrene, isoprene, and butadiene: Efficient synthesis of integral rubber containing atactic styrene–styrene sequences and high Cis‐1,4 polyconjugated olefins

SYNTHESIS OF HIGH MOLECULAR WEIGHT POLYSTYRENE WITH A RARE EARTH CATALYST

Study on a novel N-functionalized multilithium initiator and its application for preparing star-shaped N-functionalized styrene-butadiene rubber

Studies on Anionic Continuous Solution Copolymerization of Butadiene/Styrene with N-Buli Initiator

Synthesis of Primary Amine Functionalized Styrene/Butadiene Copolymer and Contol of Its Composition Distribution

Preparation of High 1,2‐orientation Butadiene‐styrene Copolymer by Coordination Copolymerization with Molybdenum‐based Catalytic System

Preparation and Dynamic Mechanical Properties of Copolymers Based on Butadiene, Isoprene, and Styrene

Study on the Structure and Mechanical Properties of SBR Prepared by High Temperature Solution Copolymerization

Effect of complex modifiers on polymerization kinetics and microstructure in synthesis of solution-polymerized styrene-butadiene rubber

Synthesis of high vinyl solution polymerized styrene-butadiene rubber with three-peak distribution using mixed coupling agents

Synthesis of High Cis-Content and Narrow Molecular Weight Distribution Polybutadiene with Neodymium Chloride Compounds Activated by Methylaluminoxane

Isospecific Polymerization of Styrene with Rare Earth Catalyst