Abstract:Ordered mesoporous carbon materials with magnetic frameworks have been synthesized via a "one-pot" block-copolymer self-assembly strategy associated with a direct carbonization process from resol, ferric citrate and triblock copolymer F127. The effects of iron loading on framework, pore features and magnetic properties of the resultant mesostructured maghemite/carbon composites were investigated by SAXS, WXRD, TEM, N-2 sorption, TG and magnetometer measurements. The results show that the mesoporous nanocomposites with a low gamma-Fe2O3 content (such as 9.0 wt%) possess an ordered 2-D hexagonal (p6mm) structure, uniform mesopores (similar to 4.0 nm), high surface areas (up to 590 m(2)/g) and pore volumes (up to 0.48 cm(3)/g). Maghemite nanocrystals with a small particle size (similar to 9.3 nm) are confined in the matrix of amorphous carbon frameworks. With the increase in gamma-Fe2O3 content, the surface area and pore volume of the nanocomposites decrease. The particle size of the gamma-Fe2O3 nanocrystals increases up to 13.1 nm. The iron oxide particles can extend from the carbon walls into mesopore channels, and hence bring a rough pore surface and gradually break down the mesoscopic regularity. The maghemite/carbon nanocomposites exhibit excellent superparamagnetic behaviors. The saturation magnetization strength can be easily adjusted from 2.5 to 12.1 emu/g by increasing the content of gamma-Fe2O3. Further H2O2 oxidation treatment of the magnetic nanocomposites endows plenty of oxygen-containing functional groups on the carbon surface, which improves their hydrophilic properties efficiently. The gamma-Fe2O3 particles, embedding into the carbon matrix, show high stability during the H2O2 oxidation process. Such modified nanocomposites with hydrophilic and magnetic framework show evidently improved adsorption properties of water and fuchsin base dye molecules in water and an easy separation procedure.

One-step Nanocasting Synthesis of Mesostructured Magnetic Fe/γ-Fe 2 O 3 /graphitic Carbon Composites

One-Step Nanocasting Route for the Synthesis of Hierarchically Mesostructured Magnetic Nanocrystalline Ni@C/Graphitic Carbon Nanocomposite and Electrochemical Performance

One‐Pot Synthesis of a Highly Active 3‐dimensional Fe−Nx−CNTs/rGO Composite Catalyst for Oxygen Reduction

A Simple Solid–liquid Grinding/templating Route for the Synthesis of Magnetic Iron/graphitic Mesoporous Carbon Composites

One-Step Nanocasting Synthesis of Ordered Mesoporous Carbon with Graphitic Frameworks

General synthesis of magnetic mesoporous FeNi/graphitic carbon nanocomposites and their application for dye adsorption

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

One-pot Synthesis of CoFe–Fe3O4 Nanocomposites with Tunable Magnetic Properties and Long Term Stability

Novel one-pot sol-gel synthesis route of Fe3C/few-layered graphene core/shell nanoparticles embedded in a carbon matrix

Preparation of SiO2/(γ-Fe2O3-SiO2 ) Magnetic Catalyst Carrier

A Facile Route to Synthesize Core/shell Structured Carbon/magnetic Nanoparticles Hybrid and Their Magnetic Properties

One-Step Method of Fabricating Fe3O4/Montmorillonite Magnetic Nanocomposites

Fe 3 O 4 nanoparticles anchoring onto graphitic carbon nitrogen nanosheets for enhanced magneto-stimuli responses and sedimentation stability

One-Pot Synthesis of Magnetically Separable Ordered Mesoporous Carbon

One-pot Solvothermal Syntheses and Magnetic Properties of Graphene-Based Magnetic Nanocomposites

Magnetite Nanostructures: One-pot Synthesis, Superparamagnetic Property and Application in Magnetic Resonance Imaging

Controlled Synthesis of Amine-Capped Γ-Fe2o3 Nanoparticles by a One-Step Process

One Step Method To Encapsulate Nanocatalysts Within Fe3o4 Nanoreactors

Controlled Synthesis of Magnetite−Silica Nanocomposites Via a Seeded Sol−Gel Approach

One-pot method fabrication of superparamagnetic sulfonated polystyrene/Fe3O4/graphene oxide micro-nano composites

Ordered mesoporous CoFe2O4 nanoparticles: molten-salt-assisted rapid nanocasting synthesis and the effects of calcining heating rate