Abstract:Halloysite/MnFe2O4 nanocomposites have been proposed as a novel material which can be used in magnetic and electromagnetic applications. In this study, we fabricated two kinds of halloysite/MnFe2O4 nanocomposites. The XRD and TEM characterizations suggested that ferrite nanoparticles were mainly adhered on the outer surface of HNTs (named as WMH) and in the inner wall (MH), respectively. Both MH and WMH were applied to adsorb methylene blue (MB) from aqueous solutions. The results indicated that both MH and WMH can remove more than 97% MB at a dosage of 2 g L-1 and initial MB concentration of 20 mg L-1. The adsorption processes by both nanocomposites fit pseudo-second-order kinetic model and Langmuir isotherm with correlation coefficient of > 0.99. WMH (19.19 mg g(-1)) shows slightly higher maximum adsorption capacity than MH (18.52 mg g(-1)), contradicts to the fact that the mesopore volume of MH is 30% larger than that of WMH. It can be reconciled by the strong bonding between the outer surface ferrite nanoparticles of WMH and the MB molecules, which greatly enhanced the MB adsorption capacity. In addition, the dimethylamino groups of MB molecules were preferably removed, suggesting the MB degradation by the ferrite nanoparticles during adsorption. Furthermore, both WMH and MH can be easily magnetic separated and recycled. The MB removal efficiency can be maintained at after regenerated for 5 times. Ascribed to the advantages of easily recycling and regeneration, low cost, and MB degradation, the halloysite-MnFe2O4 nanocomposites are potential environmental friendly adsorbents for removing organic pollutants.

One-Step Method of Fabricating Fe3O4/Montmorillonite Magnetic Nanocomposites

Adsorption of Methylene Blue by Halloysite/MnFe2O4 Nanocomposites

One-step Nanocasting Synthesis of Mesostructured Magnetic Fe/γ-Fe 2 O 3 /graphitic Carbon Composites

Preparation of Water-Soluble Magnetite Nanocrystals Through Hydrothermal Approach

Synthesis and Magnetic Properties of Mn-Zn Ferrite Nanoparticles

A facile two-step hydrothermal route for the synthesis of γ-Fe 2 O 3 nanocrystals and their magnetic properties

A new simple hydrothermal preparation of nanocrystalline magnetite Fe3O4

Preparation of superparamagnetic Fe3O4/PMMA nano composites and their magnetorheological characteristics

One-pot Synthesis of CoFe–Fe3O4 Nanocomposites with Tunable Magnetic Properties and Long Term Stability

Hydrothermal Preparation of Magnetic Fe3O4@C Nanoparticles for Dye Adsorption

Preparation and Characterization of Nylon6/cu2+-Exchanged and Fe3+-exchanged Montmorillonite Nanocomposite

Preparation of Nano-Fe3O4/Nylon Composite Fabric with Magnetic Properties by Post Finishing Method

One-step wet chemistry for preparation of magnetite nanorods

One-pot Solvothermal Syntheses and Magnetic Properties of Graphene-Based Magnetic Nanocomposites

One-step synthesis of TiO2/Fe3O4/C hydrophilic magnetic nanocomposites using the magnetized submerged arc discharge method

Preparation of CNTs-supported Fe3O4 and Fe3C Nano-particles and the Investigation on their Magnetic Properties

Magnetite Nanostructures: One-pot Synthesis, Superparamagnetic Property and Application in Magnetic Resonance Imaging

Magnetic and Electromagnetic Properties of Fe3O4/Fe Composites Prepared by a Simple One-Step Ball-Milling

One Step Synthesis of Graphene Oxide−Magnetic Nanoparticle Composite

A Simple Solution Route to Control Synthesis of Fe3O4 Nanomaterials at Low Temperature and Their Magnetic Properties

Preparation of montmorillonite nanocomposite and its adsorption