Abstract:The idea of intragranular in-situ reactions results in the proliferation of nanoreinforcements in a metal matrix composite. In this regard, high-content multi-component hybrid-reinforced 6061Al composites were synthesized in-situ from template reaction between TiO 2 -decorated carbon nanotubes (CNTs) and the matrix by flake powder metallurgy. TiO 2 nanoparticles were introduced with the help of low-amount of CNT as carrier. The total content of reinforcements increased from 3.4 wt% to ∼17.35 wt% when TiO 2 -decorated CNTs were completely reacted with the matrix, producing Al 4 C 3 /Al 4 O 4 C/Al 3 Ti/Al 2 O 3 compounds during high temperature sintering/extrusion. The as-fabricated hybrid composite exhibited outstanding mechanical properties of high tensile strength (570 MPa) and high Young's modulus (98.6 GPa) at room temperature, which were 105 % and ∼33 % higher than those of 6061Al matrix. Furthermore, the tensile strength of the hybrid-reinforced composite reached 211 MPa at 300 °C, which is about 270 % higher than the matrix. The remarkable mechanical properties were attributed to the in-situ formation of multi-components/nanophases with superior mechanical properties and high thermal stabilities. The results indicate that uniform incorporation of high-content nanophases through the in-situ reaction of nanoparticle-decorated CNTs is a promising path to produce high-performance nanocomposites and can be applied to other composite systems.

Reinforcement with In-Situ Synthesized Carbon Nano-Onions in Aluminum Composites Fabricated by Flake Powder Metallurgy

Synergistic Strengthening Effect of Graphene-Carbon Nanotube Hybrid Structure in Aluminum Matrix Composites

Reinforcement with Graphene Nanosheets in Aluminum Matrix Composites

In situ synthesis of nanostructured carbon reinforcement in aluminum powders

Uniformly Dispersed Ultrahigh-Content Nanoparticles Reinforced Aluminum Composites Achieved by Flake Dispersion Approach

Enhanced Combination of Strength and Ductility in Ultrafine-Grained Aluminum Composites Reinforced with High Content Intragranular Nanoparticles

Fabrication of Carbon Nanotube Reinforced Al Composites with Well-Balanced Strength and Ductility

Enhanced Mechanical Properties of Novel Aluminum Foams Synergistically Reinforced by NiO Particles and in Situ Grown Carbon Nanotubes

In-situ Synthesis of CNTs@Al2O3 Wrapped Structure in Aluminum Matrix Composites with Balanced Strength and Toughness

In Situ Synthesized Nano-Al4c3 Reinforced Aluminum Matrix Composites Via Friction Stir Processing

SiC and ZrN Nano-Particulate Reinforced AlON Composites: Preparation, Mechanical Properties and Toughening Mechanisms

Surface Modification of Cnts Through the Sio2 Coating to Enhance Reinforcement Penetration into Al Grain Interiors

Synergistic Strengthening of Aluminum Matrix Composites Reinforced by SiC Nanoparticles and Carbon Fibers

Reinforcement with Intragranular Dispersion of Carbon Nanotubes in Aluminum Matrix Composites

Synthesis of uniformly dispersed carbon nanotube reinforcement in Al powder for preparing reinforced Al composites

Effectively enhanced strength by interfacial reactions in in-situ carbon reinforced Al matrix composites

Design of an Efficient Flake Powder Metallurgy Route to Fabricate CNT/6061Al Composites

In-Situ Carbon Nanotube-Covered Silicon Carbide Particle Reinforced Aluminum Matrix Composites Fabricated by Powder Metallurgy

Enhanced Interfacial Bonding and Mechanical Properties in CNT/Al Composites Fabricated by Flake Powder Metallurgy

Surface Modification of CNTs Through the SiO2 Coating to Increase the Intragranular Reinforcement Content in Al Matrix Composites

Fabrication of high-content hybrid-reinforced Al nanocomposites by in-situ reaction of TiO 2 -decorated CNTs and matrix