Improvable luminescent properties by adjusting silicon–calcium stoichiometric ratio in long afterglow phosphors Ca 1.94 MgSi 2 O 7 : Eu2+0.01, Dy3+0.05

chi zhang,xinyong gong,ruirui cui,chaoyong deng

DOI: https://doi.org/10.1016/j.jallcom.2015.10.209

IF: 6.2

2016-01-01

Journal of Alloys and Compounds

Abstract:The Ca1.94MgSi2O7: Eu-0.01(2+), Dy-0.05(3+) long afterglow phosphors with different siliconecalcium stoichiometric ratios (Si/Ca = 1, 1.1, 1.2, 1.3 and 1.4) were successfully prepared under a reducing atmosphere by solid-state reaction method. The X-ray diffraction data indicate that bridging oxygen can be formed relatively easily with the increase of siliconecalcium stoichiometric ratio, which is beneficial to generating Ca2MgSi2O7, even the CaMgSi2O6 phase. Moreover, increasing the siliconecalcium stoichiometric ratio in a proper way not only reduces the sintering temperature, but also enhances the photoluminescence intensity. The afterglow properties are also improved by adjusting the siliconecalcium stoichiometric ratio, which is due to the formation of O vacancies and the codoping of Dy3+. These new insights into the Ca1.94MgSi2O7: Eu-0.01(2+), Dy-0.05(3+) phosphors with different siliconecalcium stoichiometric ratios are useful for synthesizing single akermanite phase, reducing sintering temperature and improving luminescent properties, thereby motivating the long afterglow phosphors Ca1.94MgSi2O7:Eu-0.01(2+), Dy-0.05(3+) available for commercial use. (C) 2015 Elsevier B.V. All rights reserved.