Structural, Optical, And Magnetic Properties Of (Co, Cu)-Codoped Zno Films With Different Co Concentrations

ming xu,hsiaokuan yuan,bumjae you,p f zhou,c j dong,m y duan
DOI: https://doi.org/10.1063/1.4867399
IF: 2.877
2014-01-01
Journal of Applied Physics
Abstract:Zn0.99-xCoxCu0.01O films with different Co concentrations from 0% to 20% were fabricated by a sol-gel method. Moderate Co doping is found to improve the surface uniformity and crystal quality of the films, and causes a redshift of the band edge of Zn(Co, Cu) films. X-ray photoelectron spectroscopy reveals that the introduction of Co ions causes the valence state of Cu to change from +2 to +1; while at Co concentrations lower than 10%, the Co exists in the +2 valence state. Strong blue emission at similar to 420 and 440 nm are observed, decreasing with increasing Co concentration, but becoming strong again as the concentration is increased to 20%. Enhanced room-temperature ferromagnetism is observed for the (Co, Cu)-codoped ZnO films at Co concentrations lower than 10%. These interesting magnetic properties are explained based on charge transfer, together with the defect-related model for ferromagnetism. (C) 2014 AIP Publishing LLC.
What problem does this paper attempt to address?