Abstract:In this work, the temperature-induced phase transition of (Pb0.99Nb0.02)[(Zr0.70Sn0.30)(1-x)Ti-x](0.98)O-3 (PNZST) ceramics near the morphotropic phase boundary (MPB) was investigated systematically. Increasing Ti content will stabilize the ferroelectric (FE) phase and destabilize the antiferroelectric (AFE) phase in PNZST ceramics, resulting a switching from AFE to FE. When x = 0.06, the composition has an initial AFE phase and can be induced into a stable FE phase at external electric field and when x = 0.08, the composition is normal FE. With increasing temperature, the poled PNZST sample (x = 0.06 and 0.08) will experience a ferroelectric-antiferroelectric-paraelectric (FE-AFE-PE) transition. The increasing Ti content will result in higher FE-AFE transition temperature. A step "0-1 " voltage signal up to 90 V and a current pulse can be achieved in a specific circuit when the poled ceramics were heated. An electric energy of 13.7 mJ/cm(3) was obtained during the heating process. And when the composition is closer to the AFE/FE boundary (x = 0.06), the voltage step signal is steeper because the charge release is more intensive. The special output electrical signal makes the PNZST ceramics near the MPB with potential applications for temperature sensor, tem-perature-controlled switch and temperature-driven pulsed power source. The phase transition properties can be further modified by modify the compositions near the MPB to satisfy different applications. (C) 2022 Elsevier B.V. All rights reserved.

Temperature Dependences Of Dynamic Hysteresis In Pb(Zr,Sn,Ti)O-3 Ceramics Extending Over Curie Temperature

Dynamic Hysteresis and Scaling Behavior for Pb(Zr,Ti)O3 Ceramics

Temperature Dependence of Dynamic Hysteresis Behavior in Pb0.4sr0.6tio3 Ferroelectric Films

Temperature-Dependent Ferroelectric Dynamic Hysteresis Properties of Modified Pmn-Pzt Relaxor Ceramics

Temperature-dependent Dielectric and Energy-Storage Properties of Pb(Zr,Sn,Ti)O3 Antiferroelectric Bulk Ceramics

Temperature- and Frequency-Dependent Hysteresis Scaling Behaviour and Phase Transitions in a [001]c 0.73Pb(mg1/3nb2/3)o3-0.27Pbtio3 Single Crystal

Linear Temperature Scaling of Ferroelectric Hysteresis in Mn-Doped Pb(Mn1/3sb2/3)O-3-Pb(Zr,Ti)O-3 Ceramic with Internal Bias Field

Dynamic Hysteresis and Scaling Behavior of Energy Density in Pb0.99nb0.02[(Zr0.60sn0.40)(0.95)Ti-0.05]O-3 Antiferroelectric Bulk Ceramics

Phase diagram and properties of high TC/TR-T Pb (In 1/2 Nb1/2) O3- Pb(Zn1/3 Nb 2/3) O3-PbTiO3 ferroelectric ceramics

A new (1 - X)Pb(Lu1/2Nb1/2)O3-xPbTiO 3 binary ferroelectric crystal system with high Curie temperature

Ferroelectric Phase Transition and Electrical Properties of High-Tc PMN-PH-PT Ceramics Prepared by Partial Oxalate Route

Temperature Dependences of the Ferroelectric and Dielectric Properties of High Curie Temperature PbTiO3–BiScO3–Bi(Zn1/2Zr1/2)O3

Dynamic Hysteresis Scaling of Ferroelectric Pb0.9Ba0.1(Zr0.52Ti0.48)O3 Thin Films

Effect of Temperature-Driven Phase Transition on Energy-Storage and -Release Properties of Pb0.97la0.02[Zr0.55sn0.30ti0.15]O-3 Ceramics

Temperature Scaling Behavior Of Dynamic Hysteresis For (K,Na)Nbo3 Lead-Free Ferroelectric Films

Frequency and Temperature Dependence of the Hysteresis Loop in PMnN-PZT Ceramics

Triple Hysteresis Loops of PLZST Ceramics Related to Coexistence of Ferroelectricity and Antiferroelectricity

Temperature-induced phase transition of PNZST ceramics near the morphotropic phase boundary for thermal-electrical energy conversion

Temperature Dependence of Electrical Properties of Lead Lanthanum Zirconate Stannate Titanate Ceramics

Temperature Dependence of the Dielectric, Piezoelectric, and Elastic Constants for Pb(Mg1∕3Nb2∕3)O3–PbZrO3–PbTiO3 Piezocrystals