Phase Transition Hysteresis of Ferroelectric Sr5euti3nb7o30 Ceramics with Tetragonal Tungsten Bronze Structure

Xiao Li Zhu,Xiang Ming Chen

DOI: https://doi.org/10.1063/1.3686644

IF: 2.877

2012-01-01

Journal of Applied Physics

Abstract:The first-order ferroelectric transition of Sr5EuTi3Nb7O30 tungsten bronze ceramics was investigated together with the thermal history dependence of dielectric properties and differential scanning calorimetry (DSC) analysis. Moreover, the diffuse dielectric maximum appeared at a temperature above the ferroelectric transition, and this phenomenon had been reported in ferroelectrics with perovskite structure, but had never been observed in tungsten bronzes. Large hysteresis in the ferroelectric transition and severe depression of T0 were observed in both the permittivity-temperature and DSC curves, and were attributed to the complex nature of the tetragonal tungsten bronze structure. The DSC measurements were also used to get better insight into the gradual stability of the ferroelectric phase after cooling from the high temperature paraelectric phase. The abnormal splitting of the endothermic peaks was observed during the DSC measurements with lower start temperature or longer aging time. Two possible mechanisms were suggested. One was the separation of ferroelectric phase due to the compositional inhomogeneity. In another possible mechanism, the polar nanoregions coexisting with the ferroelectric domains were suggested and would possibly transit into the paraelectric phase at temperature below the ferroelectric transition.