Giant Energy-Storage Density and Thermally Activated Phase Transition in (Pb 0.96 La 0.04 )(Zr 0.99 Ti 0.01 )O 3 Antiferroelectric Ceramics
Xiaohui Liu,Yong Li,Yangyang Li,Xihong Hao
DOI: https://doi.org/10.1021/acsaem.1c00474
IF: 6.4
2021-05-05
ACS Applied Energy Materials
Abstract:Antiferroelectric materials are regarded as potential energy storage materials due to their superior energy density during the antiferroelectric to ferroelectric phase transition. Nevertheless, their unsatisfactory energy density limits their application in practice. Herein, (Pb<sub>0.96</sub>La<sub>0.04</sub>)(Zr<sub>0.99</sub>Ti<sub>0.01</sub>)O<sub>3</sub> (PLZT) antiferroelectric ceramics are prepared via a tape-casting technique. Interestingly, the tape-casting technique can improve the ceramic microstructure, which leads to breakdown strengths ranging from 336 kV/cm for a solid state reaction to 400 kV/cm for tape-casting. A giant recoverable energy density of 11.38 J/cm<sup>3</sup> is realized at 395 kV/cm. Meanwhile, for PLZT ceramics, a high discharge energy density of 6.2 J/cm<sup>3</sup> and fast discharge speed (<i>t</i><sub>0.9</sub> = 69 ns) are achieved simultaneously under 350 kV/cm. Furthermore, the thermally activated antiferroelectric behavior is observed in <i>P–E</i> loops, and a high energy density of 8.3 J/cm<sup>3</sup> is realized at 60 °C and 310 kV/cm. Therefore, these excellent properties demonstrate that PLZT antiferroelectric materials are a potential candidate in advanced power electronic devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00474?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00474</a>.Additional data and figures including SEM images, leakage current density, Weibull distribution of BDS, and <i>P–E</i> hysteresis loops (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00474/suppl_file/ae1c00474_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels