Synthesis of metallic glasses and metallic glass based composites in the Cu-Mo-Hf system by ion beam mixing
Xue Bai,TongLe Wang,YuanYuan Cui,Ning Ding,JiaHao Li,BaiXin Liu
DOI: https://doi.org/10.1007/s11431-011-4729-x
2012-01-01
Science China Technological Sciences
Abstract:Single-phase and dual-phase metallic glasses as well as metallic glass based composites were synthesized in the Cu-Mo-Hf ternary metal system by 200 keV xenon ion beam mixing of far-from-equilibrium. It was found that Mo-Hf-based and Cu-Mo-based single-phase metallic glasses could be obtained at compositions around Cu 17 Mo 20 Hf 63 and Cu 34 Mo 57 Hf 9 , respectively. Interestingly, at the nearly equal-atomic stoichiometry of Cu 38 Mo 31 Hf 31 , a dual-phase Cu-Mo-Hf metallic glass, consisting both of the Mo-Hf-based and Cu-Mo-based phases, was first obtained at relatively low irradiation doses ranging from (1–5)×10 15 Xe + /cm 2 , and a single-phase metallic glass was eventually obtained at a dose of 7×10 15 Xe + /cm 2 . In addition, two glass-based composites were obtained at the compositions of Cu 14 Mo 62 Hf 24 and Cu 77 Mo 14 Hf 9 , and they consisted of the Mo-Hf based and Cu-Mo based metallic glasses, dissolved with some uniformly distributed BCC Mo-based and FCC Cu-based crystalline solid solutions, respectively. The formation mechanism of the above described non-equilibrium alloy phases was also discussed in terms of the atomic collision theory.