Abstract:Al2O3p/Al composites were prepared by direct melt reaction process. The thermodynamics of in situ chemical reactions between molten aluminum and CeO2 powder was studied. The XRD results show that the components of the as-prepared composites consist of Al2O3 and Al phases. For the as-cast composite specimens, SEM, EDX, TEM and SAD were used to analyze the reinforcement phases and interface characters of composites. The results show that the in situ generated Al2O3 particles, whose sizes are 100–200nm, have various irregular shapes and disperse uniformly in matrix. TEM observation shows that the interface between particle and matrix is clean. Furthermore, there is no fixed orientation relationship between Al2O3 particles and aluminum matrix. Only [12¯10]//[111] orientation parallel relationship with low exponent is found. Therefore, the composites have isotropic properties. Besides characters mentioned above, there are large amount of high density dislocations and the generated extensive fine subgrains around Al2O3 particles. These features are favorable for improving composite performances. As a result, the composites are comprehensively strengthened not only by Al2O3 particles, but also by the high density dislocations and fine subgrains.

Synthesis, Microstructure and Mechanical Properties of Cr2AlC/Al2O3 in Situ Composites by Reactive Hot Pressing

In situ (Al3Zrp+Al2O3np)/2024Al metal matrix composite with controlled reinforcement architecture fabricated by reaction hot pressing

FLEXURAL STRENGTH OF IN-SITU REACTION PROCESSED Al2O3-Al3Ti-Al COMPOSITES

In situ (Al3Zr + Al2O3np)/2024Al metal matrix composite with novel reinforcement distributions fabricated by reaction hot pressing

Reactive hot pressing and mechanical properties of TiAl3/Ti3AlC2/Al2O3 in situ composite

Microstructure and mechanical properties of Ti3(Al,Ga)C2/Al2O3 composites prepared by in situ reactive hot pressing

Microstructure and Mechanical Properties of in Situ Tial/Ti2alc Composites Prepared by Reactive Hot Pressing

Synthesis, microstructure and mechanical properties of (Ti,W) 3 AlC 2 /Al 2 O 3 composites by in situ reactive hot pressing

Synthesis and Characterization of in Situ (al 2 O 3 –si)/al Composites by Reaction Hot Pressing

Microstructural characterization and mechanical properties of TiAl–Al2Ti4C2–Al2O3–TiC in situ composites by hot-press-aided reaction synthesis

Mechanical Properties and Microstructure of Al2O3/TiAl in Situ Composites Doped with Cr

Mechanical Properties and Microstructure of Al2o3/Tial in Situ Composites Doped with Cr2o3

Microstructure and Mechanical Properties of TiC/Ti3AlC2 In Situ Composites Prepared by Hot Pressing Method

Processing, Microstructural Characterization and Mechanical Properties of in Situ Ti3AlC2/TiAl3 Composite by Hot Pressing

Microstructures and Mechanical Properties of in Situ Al 2 O 3 /Al-Si Composites Fabricated by Reaction Hot Pressing

Microstructure and Mechanical Properties of TiC/Ti<sub>3</sub>AlC<sub>2</sub> <i>In Situ</i> Composites Prepared by Hot Pressing Method

Microstructure and Mechanical Properties of Ti2AlC-reinforced TiAl Composites

Microstructure and Mechanical Property of Ti<sub>3</sub>AlC<sub>2</sub>/TiAl<sub>3</sub> Composite Synthesized by Hot Pressing

Preparation, structure, and properties of Cr2N reinforced Al2O3 composites

In situ fabrication and microstructure of Al2O3 particles reinforced aluminum matrix composites

Effect of Sintering Temperature on Microstructure and Mechanical Properties of Al2O3/TiAl In-Situ Composites