Abstract:Multi-pulse laser ablation of silver in deionized water was studied. The laser beams were arranged in a cross-beam configuration. In our experiments, two single-mode, Q-switched Nd-Yag lasers operating at 1064nm, pulse duration of 5.5ns and 10Hz rep rate were used. The laser fluence of the second beam was 0.265J/cm2 for all tests. Two levels of the laser fluences were used for the ablating beam: 0.09 and 0.265J/cm2 (11,014 and 33,042J/cm2 at the focal point, respectively). The silver target was at 50mm from the cell window and 10mm deep. The second beam was aligned parallelly with the silver target and focused at 2mm in front of the focal point of the ablating beam. For all cases, the delay time between the ablating beam and the cross-beam was 40μs. In general, the ablated particles were almost all spherical. For fluence of 0.09J/cm 2 and single-beam approach, the mean particle size was about 29nm. The majority of the particles, however, were in 19–35nm range and there were some big ones as large as 50–60nm in size. For double-beam approach, the particles were smaller with the average size of about 18nm and the majority of the particles were in 9–21nm range with few big one as large as 40nm. For the beam fluence of 0.265J/cm2 and single-beam configuration, the particle sizes were smaller, the mean particles size was about 18nm and the majority of the particles were in the range of 10–22nm with some big one as large as 40nm. For double-beam approach, the mean particle size was larger (24.2nm) and the majority of the particle were distributed from 14 to 35nm with some big particles can be found with sizes as big as 70nm. Preliminary measurements of the thermal conductivity and viscosity of the produced samples showed that the thermal conductivity increased about 3–5% and the viscosity increased 3.7% above the base fluid viscosity even with the particle volume concentration as low as 0.01%.

Nanosecond Laser Ablation Of Silver Nanoparticle Film

Nanosecond Laser Ablation of Gold Nanoparticle Films

High Resolution Selective Multilayer Laser Processing by Nanosecond Laser Ablation of Metal Nanoparticle Films

Preparation of Silver Nanoparticles Colloid by Pulsed Laser Ablation

Laser ablation of polymer-based silver nanocomposites

Ag Nanoparticles Colloids Produced by Pulsed Laser Ablation in Distilled Water

EFFECT OF SILVER NANOPARTICLE ON THE LASER ABLATION OF POLYMER

Time-resolved Analysis of Thickness-Dependent Dewetting and Ablation of Silver Films Upon Nanosecond Laser Irradiation

Characteristic Time Scales of Coalescence of Silver Nanocomposite and Nanoparticle Films Induced by Continuous Wave Laser Irradiation

Time-resolved Emission and Scattering Imaging of Plume Dynamics and Nanoparticle Ejection in Femtosecond Laser Ablation of Silver Thin Films

Optical and Morphological Properties of Silver Nanoparticles Synthesis by Q-Switched Nd-YAG Laser

Laser Wavelength Effect on Laser-Induced Photo-Thermal Sintering of Silver Nanoparticles

Laser-induced Shock Wave Sintering of Silver Nanoparticles on Flexible Substrates

Synthesis of Ag-deionized water nanofluids using multi-beam laser ablation in liquids

Femtosecond Laser Induced Ablation Dynamics Probing by Emission and Scattering Spectroscopy under Various Vacuum Conditions

Nano-particles Fabrication on Ag Film by Femtosecond Laser Direct Ablation

Femtosecond and nanosecond laser sintering of silver nanoparticles on a flexible substrate

Femtosecond laser induced photochemical reaction and configuration change of silver nanorod clusters in aqueous solution

Controllable Precipitation and Dissolution of Silver Nanoparticles in Ultrafast Laser Pulses Irradiated Ag+-doped Phosphate Glass.

Dynamics of Femtosecond Laser-Induced Melting of Silver

An Atomic-Level Study of Material Ablation and Spallation in Ultrafast Laser Processing of Gold Films