Abstract:Multi-pulse laser ablation of silver in deionized water was studied. The laser beams were arranged in a cross-beam configuration. In our experiments, two single-mode, Q-switched Nd-Yag lasers operating at 1064nm, pulse duration of 5.5ns and 10Hz rep rate were used. The laser fluence of the second beam was 0.265J/cm2 for all tests. Two levels of the laser fluences were used for the ablating beam: 0.09 and 0.265J/cm2 (11,014 and 33,042J/cm2 at the focal point, respectively). The silver target was at 50mm from the cell window and 10mm deep. The second beam was aligned parallelly with the silver target and focused at 2mm in front of the focal point of the ablating beam. For all cases, the delay time between the ablating beam and the cross-beam was 40μs. In general, the ablated particles were almost all spherical. For fluence of 0.09J/cm 2 and single-beam approach, the mean particle size was about 29nm. The majority of the particles, however, were in 19–35nm range and there were some big ones as large as 50–60nm in size. For double-beam approach, the particles were smaller with the average size of about 18nm and the majority of the particles were in 9–21nm range with few big one as large as 40nm. For the beam fluence of 0.265J/cm2 and single-beam configuration, the particle sizes were smaller, the mean particles size was about 18nm and the majority of the particles were in the range of 10–22nm with some big one as large as 40nm. For double-beam approach, the mean particle size was larger (24.2nm) and the majority of the particle were distributed from 14 to 35nm with some big particles can be found with sizes as big as 70nm. Preliminary measurements of the thermal conductivity and viscosity of the produced samples showed that the thermal conductivity increased about 3–5% and the viscosity increased 3.7% above the base fluid viscosity even with the particle volume concentration as low as 0.01%.

Preparation of Silver Nanoparticles Colloid by Pulsed Laser Ablation

Ag Nanoparticles Colloids Produced by Pulsed Laser Ablation in Distilled Water

Preparation of Ag Nanoparticles Colloid by Pulsed Laser Ablation in Distilled Water

Preparation and Size Characterization of Silver Nanoparticles Produced by Femtosecond Laser Ablation in Water

Conversion of Silver Nanoprisms into Colloidal Nanoparticles Induced by Femtosecond Laser Pulses

Nanosecond Laser Ablation Of Silver Nanoparticle Film

Formation of Silver Particles and Silver Oxide Plume Nanocomposites Upon Pulsed-Laser Induced Liquid-Solid Interface Reaction

Optical and Morphological Properties of Silver Nanoparticles Synthesis by Q-Switched Nd-YAG Laser

Preparation and optical properties of silver nanoparticles induced by a femtosecond laser irradiation

Preparation and Microstructure of Silver Nanopowder with Spheric Morphology

A Comparative Study of Silver Nanoparticles Synthesized by Arc Discharge and Femtosecond Laser Ablation in Aqueous Solution

Comparison Between Silver and Gold Nanoparticles Prepared by Pulsed Laser Ablation in Distilled Water

The Effect of Target Size on Α-Fe Nanoparticle Preparation by Pulsed Laser Ablation

Controllable Precipitation and Dissolution of Silver Nanoparticles in Ultrafast Laser Pulses Irradiated Ag+-doped Phosphate Glass.

Synthesis of Nickel-Based Nanoparticles by Pulsed Laser Ablation in Liquids: Correlations between Laser Beam Power, Size Distribution and Cavitation Bubble Lifetime

Surfactant Mediated Synthesis of Structured Metal Nanoparticle by Pulsed Laser Ablation for Photocatalysis

EFFECT OF SILVER NANOPARTICLE ON THE LASER ABLATION OF POLYMER

Synthesis of Ag-deionized water nanofluids using multi-beam laser ablation in liquids

Laser ablation of polymer-based silver nanocomposites

Laser Generation of Colloidal Nanoparticles in Liquids: Key Processes of Laser Dispersion and Main Characteristics of Nanoparticles

Development of silver nanocubes created by pulsed laser ablation in liquid